NORYL GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be electro-statically painted or powder coated without the need for a conductive primer.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高韧性耐热阻燃无卤导电易涂装 | |||
| 成型方式 | 静电/粉末喷涂 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.12 g/cm³ | ISO 1183 | |
比重 | 1.12 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/5.0 kg | 7 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300°C/5.0 kg | 7.8 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 1.3~1.5 % | Internal | flow, 3.2 mm |
吸水率 | 4 % | ISO 62 | 23°C/sat |
吸湿率 | 0.5 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 58 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 52 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 52 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 7 % | ISO 527 | 50 mm/min |
断裂(brk) | 12 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 12 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 95 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 95 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2600 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2600 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2900 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2900 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 12 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 70 J/m | ASTM D256 | |
-30℃ (-22℉) | 7 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 100 J/m | ASTM D256 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 60 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 195 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 191 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 198 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 195 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 197 °C | ISO 306 | Rate B/50 |
比热容 | 1.4 J/g-°C | ASTM C 351 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 78 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 83 E-6/°C | ISO 11359-2 | 23°C to 60°C, flow |
横向(Across Flow) | 80 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 85 E-6/°C | ISO 11359-2 | 23°C to 60°C, xflow |
导热系数 | 0.2 W/m-°C | ASTM C 177 | |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-1 | 1.5 mm | UL94 | |
V-0 | 2 mm | UL94 | |
5VB | 2 mm | UL94 | |
5VA | 2 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
2mm | 960 °C | IEC 60695-2-12 | pass |
灼热丝点燃温度(GWIT) | |||
1.0mm | 800 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 4E+3 Ohm-cm | ASTM D257 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。