NORYL GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be electro-statically painted or powder coated without the need for a conductive primer.
| Original Document | Technical Datasheet(English) | |||
| Features | Good ToughnessHeat ResistanceFlame RetardantHalogen FreeElectrically ConductiveGood Paintablility | |||
| Processing | Electrostatic/Powder Coating | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
300°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
300°C/5.0 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 3.2 mm |
Water Absorption | *** % | ISO 62 | 23°C/sat |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Yield | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 50 mm/min |
Yield | *** % | ISO 527 | 50 mm/min |
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Break | *** % | ISO 527 | 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Yield | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** J/m | ASTM D256 | |
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Instrumented Impact Energy | |||
23℃ (73℉)Total Energy | *** J | ASTM D3763 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B/50 |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | Rate B/120 |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | Rate B/50 |
Specific Heat | *** J/g-°C | ASTM C 351 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, flow |
Flow | *** E-6/°C | ISO 11359-2 | 23°C to 60°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
Across Flow | *** E-6/°C | ISO 11359-2 | 23°C to 60°C, xflow |
Thermal Conductivity | *** W/m-°C | ASTM C 177 | |
Ball Pressure Test | *** °C | IEC 60695-10-2 | PASS |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-1 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
5VB | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
2mm | *** °C | IEC 60695-2-12 | pass |
Glow Wire Ignition Test(GWIT) | |||
1.0mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.