物性表-ISO(英文) 

PBT-GB30

低翘曲

填充增强

注塑

N粘度-剪切速度 245|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|19.149:656.697@34.499:551.3440000000001@62.155:483.879@111.982:439.186@201.752:406.018@363.486:374.851@654.873:337.343@1179.85:287.552@2125.68:224.579@3829.72:154.763{n}260|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|40.825:308.025@73.55200000000001:258.603@132.515:226.959@238.745:205.998@430.135:190.44@774.951:175.821@1396.19:158.228@2515.44:134.874@4531.94:105.337@8164.97:72.59050000000001{n}275|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|82.98999999999999:151.525@149.518:127.214@269.379:111.647@485.326:101.336@874.3869999999999:93.6828@1575.34:86.49120000000001@2838.21:77.83669999999999@5113.45:66.348@9212.639999999999:51.8183@16597.9:35.7093

剪切应力-剪切速率 245|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|19.149:12575.1@34.499:19020.8@62.155:30075.5@111.982:49180.9@201.752:81915@363.486:136253@654.873:220917@1179.85:339268@2125.68:477383@3829.72:592699{n}260|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|40.825:12575.1@73.55200000000001:19020.8@132.515:30075.5@238.745:49180.9@430.135:81915.10000000001@774.951:136253@1396.19:220917@2515.44:339267@4531.94:477383@8164.97:592699{n}275|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|82.98999999999999:12575.1@149.518:19020.8@269.379:30075.4@485.326:49180.9@874.3869999999999:81915@1575.34:136253@2838.21:220917@5113.45:339267@9212.639999999999:477383@16597.9:592699

应力-应变 -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.22:12.23@0.44:23.34@0.66:33.83@0.88:43.74@1.1:52.8@1.32:60.6@1.54:66.7@1.76:70.83@1.98:73.03@2.2:73.78{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.2:10.75@0.4:20.52@0.6:29.72@0.8:38.39@1:46.33@1.2:53.18@1.4:58.59@1.6:62.31@1.8:64.33@2:64.95999999999999{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.19:9.539999999999999@0.38:18.48@0.57:26.94@0.76:34.8@0.95:41.76@1.14:47.5@1.33:51.77@1.52:54.49@1.71:55.88@1.9:56.59{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.18:8.140000000000001@0.36:15.93@0.54:23.2@0.72:29.75@0.9:35.37@1.08:39.91@1.26:43.27@1.44:45.48@1.62:46.73@1.8:47.41{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.42:11.26@0.84:19.34@1.26:24.87@1.68:28.48@2.1:30.72@2.52:32.06@2.94:32.88@3.36:33.41@3.78:33.74@4.2:33.78{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.7:8.07@1.4:13.78@2.1:17.83@2.8:20.68@3.5:22.66@4.2:24@4.9:24.84@5.6:25.31@6.3:25.56@7:25.77{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.87:7.41@1.74:12.7@2.61:16.34@3.48:18.73@4.35:20.23@5.22:21.12@6.09:21.61@6.96:21.87@7.83:21.99@8.699999999999999:22.01{n}100|%|Mpa|Strain in %|Stress in MPa|0:0@0.8100000000000001:5.78@1.62:10.15@2.43:13.31@3.24:15.49@4.05:16.93@4.86:17.83@5.67:18.39@6.48:18.73@7.29:18.94@8.1:19.02{n}120|%|Mpa|Strain in %|Stress in MPa|0:0@0.91:5.47@1.82:9.449999999999999@2.73:12.24@3.64:14.12@4.55:15.34@5.46:16.08@6.37:16.51@7.28:16.76@8.19:16.88@9.1:16.91{n}140|%|Mpa|Strain in %|Stress in MPa|0:0@0.96:4.58@1.92:7.88@2.88:10.19@3.84:11.77@4.8:12.82@5.76:13.5@6.72:13.93@7.68:14.18@8.640000000000001:14.31@9.6:14.33

正割模量-应变 -40|%|MPa|Strain in %|Secant modulus in MPa|0.22:5559.09@0.44:5304.55@0.66:5125.76@0.88:4970.45@1.1:4800@1.32:4590.91@1.54:4331.17@1.76:4024.43@1.98:3688.38@2.2:3353.64{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.2:5375@0.4:5130@0.6:4953.33@0.8:4798.75@1:4633@1.2:4431.67@1.4:4185@1.6:3894.38@1.8:3573.89@2:3248{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.19:5021.05@0.38:4863.16@0.57:4726.32@0.76:4578.95@0.95:4395.79@1.14:4166.67@1.33:3892.48@1.52:3584.87@1.71:3267.84@1.9:2978.42{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.18:4522.22@0.36:4425@0.54:4296.3@0.72:4131.94@0.9:3930@1.08:3695.37@1.26:3434.13@1.44:3158.33@1.62:2884.57@1.8:2633.89{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.42:2680.95@0.84:2302.38@1.26:1973.81@1.68:1695.24@2.1:1462.86@2.52:1272.22@2.94:1118.37@3.36:994.345@3.78:892.593@4.2:804.2859999999999{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.7:1152.86@1.4:984.2859999999999@2.1:849.048@2.8:738.571@3.5:647.429@4.2:571.429@4.9:506.939@5.6:451.964@6.3:405.714@7:368.143{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.87:851.724@1.74:729.885@2.61:626.054@3.48:538.218@4.35:465.057@5.22:404.598@6.09:354.844@6.96:314.224@7.83:280.843@8.699999999999999:252.989{n}100|%|MPa|Strain in %|Secant modulus in MPa|0.8100000000000001:713.58@1.62:626.543@2.43:547.737@3.24:478.086@4.05:418.025@4.86:366.872@5.67:324.339@6.48:289.043@7.29:259.808@8.1:234.815{n}120|%|MPa|Strain in %|Secant modulus in MPa|0.91:601.099@1.82:519.231@2.73:448.352@3.64:387.912@4.55:337.143@5.46:294.505@6.37:259.184@7.28:230.22@8.19:206.105@9.1:185.824{n}140|%|MPa|Strain in %|Secant modulus in MPa|0.96:477.083@1.92:410.417@2.88:353.819@3.84:306.51@4.8:267.083@5.76:234.375@6.72:207.292@7.68:184.635@8.640000000000001:165.625@9.6:149.271

应力-应变 (等时的)(蠕变) 23°C 1|%|MPa|Strain in %|Stress in MPa|0:0@0.0531:2@0.10732:4@0.16203:6@0.21709:8@0.27242:10@0.32796:12@0.38369:14@0.43958:16@0.49562:18@0.55178:20{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.05717:2@0.1167:4@0.1776:6@0.23968:8@0.30283:10@0.36703:12@0.43224:14@0.49848:16@0.56574:18@0.63403:20{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.0641:2@0.13298:4@0.20518:6@0.2805:8@0.35893:10@0.44056:12@0.52551:14@0.61394:16@0.70601:18@0.80194:20{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.07589:2@0.16124:4@0.25403:6@0.35428:8@0.46241:10@0.5789800000000001:12@0.70468:14@0.84027:16@0.98664:18@1.14473:20{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.09594:2@0.2103:4@0.34055:6@0.48765:8@0.65329:10@0.83955:12@1.04885:14@1.28397:16@1.54803:18@1.84454:20{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.13005:2@0.29544:4@0.49379:6@0.72872:8@1.00538:10@1.33003:12@1.70999:14@2.15376:16@2.67111:18@3.27322:20

应力-应变 (等时的)(蠕变) 40°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.3167:4@0.4285:5.3@0.5475:6.6@0.6755:7.9@0.8143:9.199999999999999@0.9656:10.5@1.1313:11.8@1.3132:13.1@1.5132:14.4@1.7871:16{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.3461:4@0.4701:5.3@0.6032:6.6@0.7476:7.9@0.9056999999999999:9.199999999999999@1.0797:10.5@1.2721:11.8@1.4851:13.1@1.7215:14.4@2.0482:16{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.3809:4@0.5194:5.3@0.6695:6.6@0.8339:7.9@1.0155:9.199999999999999@1.2173:10.5@1.4424:11.8@1.694:13.1@1.9754:14.4@2.368:16{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.4221:4@0.578:5.3@0.7486:6.6@0.9372:7.9@1.1474:9.199999999999999@1.3832:10.5@1.6485:11.8@1.9476:13.1@2.285:14.4@2.7597:16{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.4707:4@0.6476:5.3@0.8428:6.6@1.0607:7.9@1.3058:9.199999999999999@1.5832:10.5@1.8979:11.8@2.2557:13.1@2.6624:14.4@3.2394:16

应力-应变 (等时的)(蠕变) 60°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.3955:3@0.5715:4.3@0.7524999999999999:5.6@0.9409:6.9@1.1393:8.199999999999999@1.3513:9.5@1.5811:10.8@1.8339:12.1@2.1162:13.4@2.5152:15{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.4167:3@0.6029:4.3@0.7952:5.6@0.9962:6.9@1.2091:8.199999999999999@1.4379:9.5@1.6877:10.8@1.9645:12.1@2.276:13.4@2.72:15{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.4409:3@0.6388:4.3@0.844:5.6@1.0596:6.9@1.2892:8.199999999999999@1.5375:9.5@1.8104:10.8@2.1152:12.1@2.4606:13.4@2.9572:15{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.4684:3@0.6798:4.3@0.8999:5.6@1.1322:6.9@1.3811:8.199999999999999@1.652:9.5@1.9518:10.8@2.289:12.1@2.6739:13.4@3.2319:15{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.4998:3@0.7265:4.3@0.9638:5.6@1.2154:6.9@1.4866:8.199999999999999@1.7836:9.5@2.1146:10.8@2.4895:12.1@2.9205:13.4@3.55:15

应力-应变 (等时的)(蠕变) 90°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.2679:2@0.4298:3.1@0.6077:4.2@0.8051:5.3@1.0247:6.4@1.2687:7.5@1.539:8.6@1.837:9.699999999999999@2.1638:10.8@2.554:12{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.2721:2@0.4429:3.1@0.6354:4.2@0.8527:5.3@1.0966:6.4@1.3681:7.5@1.667:8.6@1.993:9.699999999999999@2.3451:10.8@2.7571:12{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.2785:2@0.4623:3.1@0.6753:4.2@0.9197:5.3@1.1953:6.4@1.5009:7.5@1.8339:8.6@2.1913:9.699999999999999@2.5695:10.8@3.0017:12{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2883:2@0.491:3.1@0.733:4.2@1.0139:5.3@1.3308:6.4@1.6785:7.5@2.0514:8.6@2.4431:9.699999999999999@2.8474:10.8@3.2962:12{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.3031:2@0.5336:3.1@0.8162:4.2@1.1466:5.3@1.5165:6.4@1.916:7.5@2.3348:8.6@2.7629:9.699999999999999@3.1916:10.8@3.6507:12

应力-应变 (等时的)(蠕变) 120°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.3815:2@0.5591:2.9@0.7444:3.8@0.9416:4.7@1.1563:5.6@1.3957:6.5@1.669:7.4@1.9878:8.300000000000001@2.3662:9.199999999999999@2.7661:10{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.395:2@0.5800999999999999:2.9@0.7749:3.8@0.9847:4.7@1.2165:5.6@1.4791:6.5@1.784:7.4@2.1449:8.300000000000001@2.579:9.199999999999999@3.0422:10{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.4129:2@0.6077:2.9@0.8147:3.8@1.0407:4.7@1.2942:5.6@1.5862:6.5@1.9307:7.4@2.3445:8.300000000000001@2.8478:9.199999999999999@3.3895:10{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.4364:2@0.6438:2.9@0.8667:3.8@1.1133:4.7@1.3944:5.6@1.7238:6.5@2.1182:7.4@2.5981:8.300000000000001@3.1876:9.199999999999999@3.8264:10{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.4674:2@0.6912:2.9@0.9344:3.8@1.2075:4.7@1.5238:5.6@1.9003:6.5@2.3576:7.4@2.9201:8.300000000000001@3.617:9.199999999999999@4.3758:10

应力-应变 (等时的)(蠕变) 160°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.5347:2@0.6539:2.4@0.7781:2.8@0.9078000000000001:3.2@1.0433:3.6@1.1847:4@1.3325:4.4@1.4868:4.8@1.6479:5.2@1.9914:6{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.5452:2@0.6702:2.4@0.8018999999999999:2.8@0.9406:3.2@1.0869:3.6@1.241:4@1.4034:4.4@1.5743:4.8@1.7542:5.2@2.1417:6{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.5590000000000001:2@0.6916:2.4@0.8329:2.8@0.9834000000000001:3.2@1.1438:3.6@1.3145:4@1.4959:4.4@1.6886:4.8@1.8929:5.2@2.338:6{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.5769:2@0.7194:2.4@0.8733:2.8@1.0393:3.2@1.2181:3.6@1.4103:4@1.6167:4.4@1.8377:4.8@2.074:5.2@2.5944:6{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.6002:2@0.7557:2.4@0.926:2.8@1.1121:3.2@1.3149:3.6@1.5354:4@1.7743:4.4@2.0324:4.8@2.3104:5.2@2.9292:6

蠕变模量-时间 23°C 5|h|MPa|Time in h|Creep modulus in MPa|1:3713.73@10:3401.06@100:2963.55@1000:2418.11@10000:1828.14@100000:1280.45{n}10|h|MPa|Time in h|Creep modulus in MPa|1:3670.8@10:3302.18@100:2786.06@1000:2162.58@10000:1530.71@100000:994.649{n}15|h|MPa|Time in h|Creep modulus in MPa|1:3644.17@10:3224.18@100:2634.84@1000:1944.95@10000:1289.64@100000:779.774{n}20|h|MPa|Time in h|Creep modulus in MPa|1:3624.63@10:3154.42@100:2493.95@1000:1747.14@10000:1084.28@100000:611.019

蠕变模量-时间 40°C 2|h|MPa|Time in h|Creep modulus in MPa|10:1290.28@100:1185.62@1000:1081.79@10000:980.602@100000:884.049{n}4|h|MPa|Time in h|Creep modulus in MPa|10:1263.02@100:1155.74@1000:1050.14@10000:947.643@100000:849.798{n}6|h|MPa|Time in h|Creep modulus in MPa|10:1220.58@100:1110.07@1000:1002.31@10000:898.427@100000:799.819{n}8|h|MPa|Time in h|Creep modulus in MPa|10:1166.57@100:1053.68@1000:944.264@10000:839.849@100000:741.753{n}10|h|MPa|Time in h|Creep modulus in MPa|10:1103.98@100:989.373@1000:879.423@10000:775.647@100000:679.167{n}12|h|MPa|Time in h|Creep modulus in MPa|10:1036.08@100:920.601@1000:811.17@10000:709.111@100000:615.364{n}14|h|MPa|Time in h|Creep modulus in MPa|10:965.982@100:850.6950000000001@1000:742.746@10000:643.3390000000001@100000:553.1849999999999{n}16|h|MPa|Time in h|Creep modulus in MPa|10:895.3049999999999@100:781.174@1000:675.676@10000:579.773@100000:493.919

蠕变模量-时间 60°C 2|h|MPa|Time in h|Creep modulus in MPa|10:761.827@100:723.545@1000:684.359@10000:644.8@100000:604.768{n}4|h|MPa|Time in h|Creep modulus in MPa|10:753.9930000000001@100:714.967@1000:675.021@10000:634.576@100000:594.038{n}6|h|MPa|Time in h|Creep modulus in MPa|10:741.136@100:700.949@1000:660.011@10000:618.628@100000:577.217{n}8|h|MPa|Time in h|Creep modulus in MPa|10:722.03@100:680.607@1000:638.576@10000:596.338@100000:554.26{n}10|h|MPa|Time in h|Creep modulus in MPa|10:695.758@100:653.106@1000:610.081@10000:567.088@100000:524.575{n}12|h|MPa|Time in h|Creep modulus in MPa|10:661.679@100:617.867@1000:574.016@10000:530.591@100000:488.007{n}14|h|MPa|Time in h|Creep modulus in MPa|10:619.206@100:574.528@1000:530.289@10000:486.926@100000:444.84{n}15|h|MPa|Time in h|Creep modulus in MPa|10:596.374@100:551.471@1000:507.237@10000:464.123@100000:422.535

蠕变模量-时间 90°C 2|h|MPa|Time in h|Creep modulus in MPa|10:746.547@100:735.024@1000:718.133@10000:693.722@100000:659.848{n}4|h|MPa|Time in h|Creep modulus in MPa|10:696.864@100:668.188@1000:630.6369999999999@10000:583.026@100000:525.549{n}6|h|MPa|Time in h|Creep modulus in MPa|10:636.854@100:597.167@1000:549.6900000000001@10000:495.169@100000:435.402{n}8|h|MPa|Time in h|Creep modulus in MPa|10:576.292@100:533.134@1000:485.135@10000:433.546@100000:380.119{n}10|h|MPa|Time in h|Creep modulus in MPa|10:520.018@100:479.31@1000:436.218@10000:391.796@100000:347.196{n}12|h|MPa|Time in h|Creep modulus in MPa|10:469.851@100:435.24@1000:399.773@10000:364.056@100000:328.704

蠕变模量-时间 120°C 2|h|MPa|Time in h|Creep modulus in MPa|10:524.246@100:506.329@1000:484.379@10000:458.295@100000:427.899{n}4|h|MPa|Time in h|Creep modulus in MPa|10:508.247@100:487.802@1000:463.494@10000:435.2@100000:403.19{n}6|h|MPa|Time in h|Creep modulus in MPa|10:476.505@100:451.536@1000:422.988@10000:391.148@100000:356.593{n}8|h|MPa|Time in h|Creep modulus in MPa|10:426.448@100:396.483@1000:363.944@10000:329.521@100000:294.135{n}10|h|MPa|Time in h|Creep modulus in MPa|10:361.52@100:328.709@1000:295.029@10000:261.342@100000:228.53

蠕变模量-时间 160°C 1|h|MPa|Time in h|Creep modulus in MPa|10:387.029@100:383.184@1000:378.311@10000:372.191@100000:364.662{n}2|h|MPa|Time in h|Creep modulus in MPa|10:374.042@100:366.838@1000:357.782@10000:346.681@100000:333.222{n}3|h|MPa|Time in h|Creep modulus in MPa|10:356.196@100:344.696@1000:330.779@10000:314.223@100000:294.982{n}4|h|MPa|Time in h|Creep modulus in MPa|10:337.638@100:322.321@1000:304.298@10000:283.628@100000:260.518{n}5|h|MPa|Time in h|Creep modulus in MPa|10:319.211@100:300.669@1000:279.475@10000:255.933@100000:230.573{n}6|h|MPa|Time in h|Creep modulus in MPa|10:301.296@100:280.151@1000:256.63@10000:231.267@100000:204.834

拉伸模量-温度 |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:5458@-30:5309@-20:5160@-10:4967@0:4750@10:4606@20:4413@30:3874@40:2290@50:1493@60:1159@70:983@80:871@90:789@100:706@110:642@120:585@130:530@140:463

30% 玻璃微珠