| 原厂资料 | 物性表-ASTM(英文) 物性表-ISO(英文) | |||
| 缩写标识 | PA6 | |||
| 产品特性 | 热稳定耐磨耐化学性低粘度 | |||
| 成型方式 | 注塑 | |||
| 汽车材料标准 | 福特(FORD) WSK-M4D672-A通用(GM) GMW17173P-PA6斯泰兰蒂斯(Stellantis) MS-DB-41 | |||
| 曲线坐标 | N粘度-剪切速度剪切应力-剪切速率动态剪切模量 (G 储能)-温度应力-应变正割模量-应变 | |||
| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
|---|---|---|---|
密度/比重 | *** g/cm³ | ISO 1183 | |
密度/比重 | *** g/cm³ | ASTM D792 | |
收缩率 | |||
- | *** % | Internal | |
吸水率 | *** % | ASTM D570 | 24 hr |
吸水率 | *** % | ASTM D570 | 50% RH |
吸水率 | *** % | ASTM D570 | Saturation |
吸水率 | *** % | ISO 62 | 24 hr |
吸水率 | *** % | ISO 62 | 50% RH |
吸水率 | *** % | ISO 62 | Saturation |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 | *** Mpa | ISO 527 | Conditioned,120℃ |
拉伸模量 | *** Mpa | ISO 527 | Conditioned,150℃ |
拉伸模量 | *** Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | *** Mpa | ISO 527 | Conditioned,80℃ |
拉伸模量 | *** Mpa | ISO 527 | Dry,120℃ |
拉伸模量 | *** Mpa | ISO 527 | Dry,150℃ |
拉伸模量 | *** Mpa | ISO 527 | Dry,23℃ |
拉伸模量 | *** Mpa | ISO 527 | Dry,80℃ |
拉伸强度 | |||
屈服(yld) | *** Mpa | ASTM D638 | Conditioned,-40℃ |
屈服(yld) | *** Mpa | ASTM D638 | Conditioned,121℃ |
屈服(yld) | *** Mpa | ASTM D638 | Conditioned,23℃ |
屈服(yld) | *** Mpa | ASTM D638 | Conditioned,80℃ |
屈服(yld) | *** Mpa | ASTM D638 | Dry,-40℃ |
屈服(yld) | *** Mpa | ASTM D638 | Dry,121℃ |
屈服(yld) | *** Mpa | ASTM D638 | Dry,23℃ |
屈服(yld) | *** Mpa | ASTM D638 | Dry,80℃ |
屈服(yld) | *** Mpa | ISO 527 | Conditioned,-40℃ |
屈服(yld) | *** Mpa | ISO 527 | Conditioned,120℃ |
屈服(yld) | *** Mpa | ISO 527 | Conditioned,150℃ |
屈服(yld) | *** Mpa | ISO 527 | Conditioned,23℃ |
屈服(yld) | *** Mpa | ISO 527 | Conditioned,80℃ |
屈服(yld) | *** Mpa | ISO 527 | Dry,-40℃ |
屈服(yld) | *** Mpa | ISO 527 | Dry,120℃ |
屈服(yld) | *** Mpa | ISO 527 | Dry,150℃ |
屈服(yld) | *** Mpa | ISO 527 | Dry,23℃ |
屈服(yld) | *** Mpa | ISO 527 | Dry,80℃ |
断裂(brk) | *** Mpa | ASTM D638 | Conditioned,23℃ |
断裂(brk) | *** Mpa | ASTM D638 | Dry,23℃ |
拉伸延伸率 | |||
屈服(yld) | *** % | ASTM D638 | Conditioned,121℃ |
屈服(yld) | *** % | ASTM D638 | Conditioned,23℃ |
屈服(yld) | *** % | ASTM D638 | Conditioned,80℃ |
屈服(yld) | *** % | ASTM D638 | Dry,121℃ |
屈服(yld) | *** % | ASTM D638 | Dry,23℃ |
屈服(yld) | *** % | ASTM D638 | Dry,80℃ |
屈服(yld) | *** % | ISO 527 | Conditioned,23℃ |
屈服(yld) | *** % | ISO 527 | Dry,23℃ |
断裂(brk) | *** % | ASTM D638 | Conditioned,23℃ |
断裂(brk) | *** % | ASTM D638 | Dry,23℃ |
标称断裂伸长率 | *** % | ISO 527 | Conditioned,23℃ |
标称断裂伸长率 | *** % | ISO 527 | Dry,23℃ |
弯曲模量 | *** Mpa | ASTM D790 | Conditioned,-40℃ |
弯曲模量 | *** Mpa | ASTM D790 | Conditioned,23℃ |
弯曲模量 | *** Mpa | ASTM D790 | Dry,-40℃ |
弯曲模量 | *** Mpa | ASTM D790 | Dry,121℃ |
弯曲模量 | *** Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | *** Mpa | ASTM D790 | Dry,65℃ |
弯曲模量 | *** Mpa | ASTM D790 | Dry,90℃ |
弯曲模量 | *** Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | *** Mpa | ISO 178 | Dry,23℃ |
弯曲强度 | |||
- | *** Mpa | ASTM D790 | Conditioned,-40℃ |
- | *** Mpa | ASTM D790 | Conditioned,23℃ |
- | *** Mpa | ASTM D790 | Dry,-40℃ |
- | *** Mpa | ASTM D790 | Dry,121℃ |
- | *** Mpa | ASTM D790 | Dry,23℃ |
- | *** Mpa | ASTM D790 | Dry,65℃ |
- | *** Mpa | ASTM D790 | Dry,90℃ |
- | *** Mpa | ISO 178 | Conditioned,23℃ |
- | *** Mpa | ISO 178 | Dry,23℃ |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | *** J/m | ASTM D256 | Conditioned |
-40℃ (-40℉) | *** J/m | ASTM D256 | Dry |
23℃ (73℉) | *** J/m | ASTM D256 | Conditioned |
23℃ (73℉) | *** J/m | ASTM D256 | Dry |
落锤冲击 | *** J | Internal | Conditioned,23℃ |
落锤冲击 | *** J | Internal | Dry |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
洛氏硬度R | *** R | ASTM D785 | Dry |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | Dry |
相对温度指数(RTI), 冲击Imp | |||
0.71mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
相对温度指数(RTI), 电气Elec | |||
0.71mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
相对温度指数(RTI), 强度Str | |||
0.71mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
线性膨胀系数(CLTE) | |||
- | *** E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | *** °C | ASTM D3418 | Dry |
熔融温度(Tm) | *** °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
防火等级 | |||
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
| 电学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
体积电阻率 | *** Ohm-m | ASTM D257 | Dry,1.50 mm |
体积电阻率 | *** Ohm-m | IEC 60093 | Dry |
相对漏电起痕指数(CTI) | |||
- | *** V | IEC 60112 | Dry |
绝缘强度 | *** kV/mm | ASTM D149 | Dry,1.50 mm,Short-Time |
绝缘强度 | *** kV/mm | IEC 60243-1 | Dry |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。