Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose PA6 injection molding. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas.
Applications
Ultramid 8202 HS is generally recommended for drapery hardware, gears, fittings, furniture casters, bearings, handles, clips, fasteners and thin parts.
| Original Document | Technical Datasheet-ASTM(English) Technical Datasheet-ISO(English) | |||
| Resin ID | PA6 | |||
| Features | Heat StabilizedWear/Abrasion ResistanceChemical ResistanceLow viscosity | |||
| Processing | Injection | |||
| Automotive Specs | FORD WSK-M4D672-AGM(General Motors) GMW17173P-PA6Stellantis MS-DB-41 | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateDynamic Shear modulus (G storage)-temperatureStress-strainSecant modulus-strain | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
- | *** % | Internal | |
Water Absorption | *** % | ASTM D570 | 24 hr |
Water Absorption | *** % | ASTM D570 | 50% RH |
Water Absorption | *** % | ASTM D570 | Saturation |
Water Absorption | *** % | ISO 62 | 24 hr |
Water Absorption | *** % | ISO 62 | 50% RH |
Water Absorption | *** % | ISO 62 | Saturation |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | Conditioned,120℃ |
Tensile Modulus | *** Mpa | ISO 527 | Conditioned,150℃ |
Tensile Modulus | *** Mpa | ISO 527 | Conditioned,23℃ |
Tensile Modulus | *** Mpa | ISO 527 | Conditioned,80℃ |
Tensile Modulus | *** Mpa | ISO 527 | Dry,120℃ |
Tensile Modulus | *** Mpa | ISO 527 | Dry,150℃ |
Tensile Modulus | *** Mpa | ISO 527 | Dry,23℃ |
Tensile Modulus | *** Mpa | ISO 527 | Dry,80℃ |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Conditioned,-40℃ |
Yield | *** Mpa | ASTM D638 | Conditioned,121℃ |
Yield | *** Mpa | ASTM D638 | Conditioned,23℃ |
Yield | *** Mpa | ASTM D638 | Conditioned,80℃ |
Yield | *** Mpa | ASTM D638 | Dry,-40℃ |
Yield | *** Mpa | ASTM D638 | Dry,121℃ |
Yield | *** Mpa | ASTM D638 | Dry,23℃ |
Yield | *** Mpa | ASTM D638 | Dry,80℃ |
Yield | *** Mpa | ISO 527 | Conditioned,-40℃ |
Yield | *** Mpa | ISO 527 | Conditioned,120℃ |
Yield | *** Mpa | ISO 527 | Conditioned,150℃ |
Yield | *** Mpa | ISO 527 | Conditioned,23℃ |
Yield | *** Mpa | ISO 527 | Conditioned,80℃ |
Yield | *** Mpa | ISO 527 | Dry,-40℃ |
Yield | *** Mpa | ISO 527 | Dry,120℃ |
Yield | *** Mpa | ISO 527 | Dry,150℃ |
Yield | *** Mpa | ISO 527 | Dry,23℃ |
Yield | *** Mpa | ISO 527 | Dry,80℃ |
Break | *** Mpa | ASTM D638 | Conditioned,23℃ |
Break | *** Mpa | ASTM D638 | Dry,23℃ |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Conditioned,121℃ |
Yield | *** % | ASTM D638 | Conditioned,23℃ |
Yield | *** % | ASTM D638 | Conditioned,80℃ |
Yield | *** % | ASTM D638 | Dry,121℃ |
Yield | *** % | ASTM D638 | Dry,23℃ |
Yield | *** % | ASTM D638 | Dry,80℃ |
Yield | *** % | ISO 527 | Conditioned,23℃ |
Yield | *** % | ISO 527 | Dry,23℃ |
Break | *** % | ASTM D638 | Conditioned,23℃ |
Break | *** % | ASTM D638 | Dry,23℃ |
Nominal Tensile Strain at Break | *** % | ISO 527 | Conditioned,23℃ |
Nominal Tensile Strain at Break | *** % | ISO 527 | Dry,23℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Conditioned,-40℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Conditioned,23℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Dry,-40℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Dry,121℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Dry,23℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Dry,65℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Dry,90℃ |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned,23℃ |
Flexural Modulus | *** Mpa | ISO 178 | Dry,23℃ |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | Conditioned,-40℃ |
- | *** Mpa | ASTM D790 | Conditioned,23℃ |
- | *** Mpa | ASTM D790 | Dry,-40℃ |
- | *** Mpa | ASTM D790 | Dry,121℃ |
- | *** Mpa | ASTM D790 | Dry,23℃ |
- | *** Mpa | ASTM D790 | Dry,65℃ |
- | *** Mpa | ASTM D790 | Dry,90℃ |
- | *** Mpa | ISO 178 | Conditioned,23℃ |
- | *** Mpa | ISO 178 | Dry,23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** J/m | ASTM D256 | Conditioned |
-40℃ (-40℉) | *** J/m | ASTM D256 | Dry |
23℃ (73℉) | *** J/m | ASTM D256 | Conditioned |
23℃ (73℉) | *** J/m | ASTM D256 | Dry |
Falling Dart Impact | *** J | Internal | Conditioned,23℃ |
Falling Dart Impact | *** J | Internal | Dry |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | Dry |
Relative Temperature Index(RTI), Imp | |||
0.71mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.71mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
0.71mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6 mm/mm/℃ | ASTM D E831 | Dry |
Melt Temperature(Tm) | *** °C | ASTM D3418 | Dry |
Melt Temperature(Tm) | *** °C | ISO 3146 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | ASTM D257 | Dry,1.50 mm |
Volume Resistivity | *** Ohm-m | IEC 60093 | Dry |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | Dry |
Dielectric Strength | *** kV/mm | ASTM D149 | Dry,1.50 mm,Short-Time |
Dielectric Strength | *** kV/mm | IEC 60243-1 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.