| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击耐热良好表面高光泽易着色高流动 | |||
| 应用产品 | 玩具家居用品外壳家用电器汽车零部件卫浴洁具 | |||
| 成型方式 | 注塑 | |||
| 曲线坐标 | N粘度-剪切速度 210|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|10.876:3614.99@19.595:2712.48@35.303:2016.69@63.604:1471.81@114.593:1047.46@206.456:724.145@371.962:485.754@670.144:316.677@1207.36:201.516@2175.25:126.059{n}245|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|70.027:561.449@126.164:421.285@227.303:313.218@409.52:228.592@737.8099999999999:162.687@1329.28:112.47@2394.89:75.4448@4314.75:49.1845@7773.66:31.2984@14005.4:19.5789{n}280|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|192.259:204.498@346.384:153.445@624.062:114.084@1124.34:83.2604@2025.67:59.2555@3649.54:40.9652@6575.19:27.4794@11846.2:17.9145@21342.7:11.3998@38452:7.13125剪切应力-剪切速率 210|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|10.876:39316.6@19.595:53151@35.303:71195.3@63.604:93613@114.593:120032@206.456:149504@371.962:180682@670.144:212219@1207.36:243302@2175.25:274210{n}245|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|70.027:39316.6@126.164:53151@227.303:71195.3@409.52:93613@737.8099999999999:120032@1329.28:149504@2394.89:180682@4314.75:212219@7773.66:243303@14005.4:274211{n}280|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|192.259:39316.6@346.384:53151@624.062:71195.3@1124.34:93613@2025.67:120032@3649.54:149504@6575.19:180682@11846.2:212219@21342.7:243303@38452:274211动态剪切模量-温度 G'|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-60:1008.9@-50:985.1@-40:963.8@-30:946.1@-20:928.1@-10:912.1@0:894.9@10:876@20:856.5@30:836@40:812@50:785.2@60:756@70:724.9@80:686@90:625@100:467.6@110:57.6@120:1.8@130:0.8@140:0.5@150:0.4{n}G"|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-60:18.5436@-50:17.7219@-40:16.8279@-30:16.2918@-20:16.019@-10:15.6972@0:15.3028@10:15.4702@20:15.3913@30:15.5914@40:16.9627@50:18.7113@60:20.7673@70:23.5085@80:28.9149@90:41.6@100:84.82259999999999@110:81.9072@120:2.8044@130:0.43464@140:0.1459@150:0.16116{n}tan d|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-60:0.01838@-50:0.01799@-40:0.01746@-30:0.01722@-20:0.01726@-10:0.01721@0:0.0171@10:0.01766@20:0.01797@30:0.01865@40:0.02089@50:0.02383@60:0.02747@70:0.03243@80:0.04215@90:0.06655999999999999@100:0.1814@110:1.422@120:1.558@130:0.5433@140:0.2918@150:0.4029应力-应变 -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.36:10.12@0.72:19.48@1.08:28.05@1.44:35.82@1.8:42.82@2.16:49.02@2.52:54.36@2.88:58.72@3.24:61.84@3.6:63.34{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.31:8.460000000000001@0.62:16.47@0.93:23.96@1.24:30.9@1.55:37.25@1.86:42.95@2.17:47.91@2.48:51.99@2.79:54.97@3.1:56.56{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.3:8.07@0.6:15.19@0.9:21.77@1.2:27.9@1.5:33.5@1.8:38.32@2.1:42.14@2.4:44.76@2.7:46.16@3:46.57{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.23:5.76@0.46:11.25@0.6899999999999999:16.45@0.92:21.33@1.15:25.87@1.38:30.04@1.61:33.77@1.84:36.94@2.07:39.38@2.3:40.82{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.22:5.14@0.44:10.08@0.66:14.75@0.88:19.09@1.1:23.03@1.32:26.49@1.54:29.42@1.76:31.71@1.98:33.26@2.2:33.94{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.23:4.78@0.46:9.300000000000001@0.6899999999999999:13.45@0.92:17.13@1.15:20.23@1.38:22.68@1.61:24.46@1.84:25.61@2.07:26.23@2.3:26.55{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.24:4.25@0.48:7.99@0.72:11.2@0.96:13.88@1.2:15.99@1.44:17.53@1.68:18.52@1.92:19.05@2.16:19.27@2.4:19.45正割模量-应变 -40|%|MPa|Strain in %|Secant modulus in MPa|0.36:2811.11@0.72:2705.56@1.08:2597.22@1.44:2487.5@1.8:2378.89@2.16:2269.44@2.52:2157.14@2.88:2038.89@3.24:1908.64@3.6:1759.44{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.31:2729.03@0.62:2656.45@0.93:2576.34@1.24:2491.94@1.55:2403.23@1.86:2309.14@2.17:2207.83@2.48:2096.37@2.79:1970.25@3.1:1824.52{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.3:2690@0.6:2531.67@0.9:2418.89@1.2:2325@1.5:2233.33@1.8:2128.89@2.1:2006.67@2.4:1865@2.7:1709.63@3:1552.33{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.23:2504.35@0.46:2445.65@0.6899999999999999:2384.06@0.92:2318.48@1.15:2249.57@1.38:2176.81@1.61:2097.52@1.84:2007.61@2.07:1902.42@2.3:1774.78{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.22:2336.36@0.44:2290.91@0.66:2234.85@0.88:2169.32@1.1:2093.64@1.32:2006.82@1.54:1910.39@1.76:1801.7@1.98:1679.8@2.2:1542.73{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.23:2078.26@0.46:2021.74@0.6899999999999999:1949.28@0.92:1861.96@1.15:1759.13@1.38:1643.48@1.61:1519.25@1.84:1391.85@2.07:1267.15@2.3:1154.35{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.24:1770.83@0.48:1664.58@0.72:1555.56@0.96:1445.83@1.2:1332.5@1.44:1217.36@1.68:1102.38@1.92:992.188@2.16:892.13@2.4:810.417应力-应变 (等时的)(蠕变) 23°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1464:3@0.23:4.7@0.3142:6.4@0.3995:8.1@0.4862:9.800000000000001@0.5750999999999999:11.5@0.6669:13.2@0.7625:14.9@0.8633999999999999:16.6@0.9516:18{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.1608:3@0.2534:4.7@0.3479:6.4@0.4448:8.1@0.5452:9.800000000000001@0.6505:11.5@0.7625:13.2@0.8836000000000001:14.9@1.0168:16.6@1.1382:18{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.1895:3@0.3009:4.7@0.4166:6.4@0.5382:8.1@0.668:9.800000000000001@0.8090000000000001:11.5@0.9654:13.2@1.1428:14.9@1.3481:16.6@1.5447:18{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2472:3@0.3971:4.7@0.5572:6.4@0.731:8.1@0.9236:9.800000000000001@1.142:11.5@1.3957:13.2@1.6975:14.9@2.064:16.6@2.4295:18{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.3629:3@0.5918:4.7@0.8443000000000001:6.4@1.1284:8.1@1.4556:9.800000000000001@1.8416:11.5@2.3082:13.2@2.8848:14.9@3.6105:16.6@4.3558:18应力-应变 (等时的)(蠕变) 60°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1132:1.5@0.2058:2.7@0.3016:3.9@0.4023:5.1@0.5098:6.3@0.6266:7.5@0.7558:8.699999999999999@0.9011:9.9@1.0674:11.1@1.2953:12.5{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.1559:1.5@0.2855:2.7@0.4222:3.9@0.5695:5.1@0.7314000000000001:6.3@0.9132:7.5@1.1214:8.699999999999999@1.3643:9.9@1.6518:11.1@2.0604:12.5{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.2393:1.5@0.4419:2.7@0.6604:3.9@0.9016:5.1@1.1741:6.3@1.489:7.5@1.8602:8.699999999999999@2.3051:9.9@2.8457:11.1@3.6335:12.5{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.4022:1.5@0.7492:2.7@1.1309:3.9@1.5613:5.1@2.0585:6.3@2.6457:7.5@3.3524:8.699999999999999@4.2162:9.9@5.2843:11.1@6.8677:12.5{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.7205:1.5@1.353:2.7@2.0604:3.9@2.8719:5.1@3.8253:6.3@4.9693:7.5@6.3669:8.699999999999999@8.0984:9.9@10.2657:11.1@13.5171:12.5蠕变模量-时间 23°C 5|h|MPa|Time in h|Creep modulus in MPa|10:2042.45@100:1852.36@1000:1557.77@10000:1177.75@100000:788.042{n}10|h|MPa|Time in h|Creep modulus in MPa|10:2013.98@100:1794.35@1000:1462.12@10000:1055.07@100000:667.731{n}15|h|MPa|Time in h|Creep modulus in MPa|10:1952.46@100:1683.42@1000:1299.86@10000:873.6420000000001@100000:513.239{n}18|h|MPa|Time in h|Creep modulus in MPa|10:1891.55@100:1581.44@1000:1165.27@10000:740.893@100000:413.242蠕变模量-时间 60°C 2|h|MPa|Time in h|Creep modulus in MPa|10:1320.33@100:956.059@1000:620.925@10000:368.2@100000:204.887{n}4|h|MPa|Time in h|Creep modulus in MPa|10:1291.24@100:921.62@1000:588.646@10000:343.441@100000:188.361{n}6|h|MPa|Time in h|Creep modulus in MPa|10:1244.4@100:870.473@1000:544.235@10000:311.407@100000:168.014{n}8|h|MPa|Time in h|Creep modulus in MPa|10:1178.71@100:803.021@1000:489.064@10000:273.657@100000:145.033{n}10|h|MPa|Time in h|Creep modulus in MPa|10:1094.08@100:721.373@1000:426.289@10000:232.777@100000:121.077{n}12|h|MPa|Time in h|Creep modulus in MPa|10:990.6180000000001@100:628.615@1000:359.248@10000:191.181@100000:97.55029999999999比容-温度(pvT) 0.1|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.95931@30:0.96272@40:0.96613@50:0.96954@60:0.97295@70:0.97636@80:0.97977@90:0.9831800000000001@100:0.98659@110:0.99@120:0.99613@130:1.00226@140:1.00839@150:1.01452@160:1.02065@170:1.02678@180:1.03291@190:1.03904@200:1.04517@210:1.0513@220:1.05743@230:1.06356@240:1.06969@250:1.07582@260:1.08195@270:1.08808{n}40|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.94998@30:0.95289@40:0.95578@50:0.95863@60:0.96146@70:0.96426@80:0.9670299999999999@90:0.96977@100:0.97248@110:0.97515@115.52:0.97585@120:0.97822@130:0.98347@140:0.98868@150:0.99385@160:0.99898@170:1.00407@180:1.00911@190:1.01411@200:1.01905@210:1.02395@220:1.0288@230:1.0336@240:1.03834@250:1.04303@260:1.04766@270:1.05223{n}80|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.94157@30:0.94407@40:0.94653@50:0.94895@60:0.9513200000000001@70:0.95364@80:0.95592@90:0.95814@100:0.96032@110:0.96244@120:0.96451@121.04:0.96379@130:0.96794@140:0.97251@150:0.97703@160:0.98148@170:0.98587@180:0.9902@190:0.99447@200:0.9986699999999999@210:1.0028@220:1.00686@230:1.01085@240:1.01477@250:1.01862@260:1.0224@270:1.0261{n}120|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.93391@30:0.93607@40:0.93818@50:0.94023@60:0.94223@70:0.94417@80:0.9460499999999999@90:0.94787@100:0.94963@110:0.95133@120:0.95296@126.56:0.95328@130:0.9547099999999999@140:0.9588100000000001@150:0.96284@160:0.9668099999999999@170:0.9707@180:0.9745200000000001@190:0.97827@200:0.98194@210:0.98554@220:0.9890600000000001@230:0.99251@240:0.99588@250:0.99917@260:1.00238@270:1.00552{n}160|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.92688@30:0.92875@40:0.93057@50:0.93232@60:0.93401@70:0.93563@80:0.93719@90:0.93868@100:0.9401@110:0.94146@120:0.94274@130:0.94395@132.08:0.94397@140:0.94692@150:0.95058@160:0.95417@170:0.95768@180:0.96111@190:0.96447@200:0.96776@210:0.97096@220:0.97409@230:0.97714@240:0.98011@250:0.983@260:0.98581@270:0.98854{n}200|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.92038@30:0.92201@40:0.92357@50:0.92506@60:0.92649@70:0.92785@80:0.92914@90:0.93036@100:0.9315@110:0.93258@120:0.93358@130:0.9345@137.6:0.9356@140:0.93641@150:0.9397799999999999@160:0.94307@170:0.94628@180:0.94941@190:0.95247@200:0.95545@210:0.95835@220:0.96117@230:0.96391@240:0.96657@250:0.96916@260:0.97166@270:0.97409拉伸模量-温度 |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:2764@-30:2737@-20:2703@-10:2609@0:2473@10:2456@20:2408@30:2309@40:2186@50:2039@60:1834@70:1651@80:1487 | |||
| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
|---|---|---|---|
密度/比重 | *** g/cm³ | ISO 1183 | |
密度/比重 | *** g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
220°C/10.0 kg | *** cm³/10 min | ISO 1133 | |
230℃/3.8 kg | *** cm³/10 min | ASTM D 1238 | |
熔体质量流动速率(MFR) | |||
200 ℃/5 Kg | *** g/10 min | ASTM D 1238 | |
220℃/10 kg | *** g/10 min | ASTM D 1238 | |
收缩率 | |||
- | ***~*** in/in | ASTM D955 | |
- | ***~*** % | ISO 294-4 | |
吸水率 | *** % | ASTM D570 | Saturated at 23 °C |
吸水率 | *** % | ISO 62 | Saturated at 23 °C |
吸湿率 | *** % | ISO 62 | Equilibrium 23 °C/50% RH |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 | *** psi | ASTM D638 | |
拉伸模量 | *** Mpa | ISO 527 | |
拉伸强度 | |||
屈服(yld) | *** psi | ASTM D638 | 23 °C |
屈服(yld) | *** Mpa | ISO 527 | |
拉伸延伸率 | |||
屈服(yld) | *** % | ISO 527 | |
标称断裂伸长率 | *** % | ISO 527 | |
- | *** % | ASTM D 638 | |
弯曲模量 | *** psi | ASTM D790 | 23 °C |
弯曲强度 | |||
- | *** psi | ASTM D790 | 23 °C |
- | *** Mpa | ISO 178 | |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | *** ft·lb/in | ASTM D256 | |
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
-18℃ (0℉) | *** ft·lb/in | ASTM D 256 | |
23℃ (73℉) | *** ft·lb/in | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
洛氏硬度R | *** R | ASTM D785 | |
球压硬度 | *** Mpa | ISO 2039-1 | |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °F | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °F | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °F | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °F | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | annealed 4 h/80 °C |
维卡软化温度(Vicat) | *** °F | ISO 306 | VST/A/50 (10N, 50 °C/h) |
维卡软化温度(Vicat) | *** °C | ISO 306 | VST/A/50 (10N, 50 °C/h) |
维卡软化温度(Vicat) | *** °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
线性膨胀系数(CLTE) | |||
- | ***~*** E-6/°C | ISO 11359 | |
导热系数 | *** W/(m K) | DIN 52612-1 | |
加工温度 | ***~*** °C | - | |
模具温度 | ***~*** °C | - | |
| 电学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
体积电阻率 | > *** Ohm-m | ASTM D257 | |
体积电阻率 | > *** Ohm-m | IEC 60093 | |
表面电阻率 | > *** Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
1MHz | *** - | ASTM D 150 | 0,0394 in |
耗散因数(DF) | |||
100Hz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | |
| 其他性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
黄色指数(YI) | *** - | DIN 6167 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。
| 中文名 | 英文名 | 文件格式 | 操作 |
|---|---|---|---|
| 物性表-ISO(英文) | Technical Datasheet-ISO(English) | 下载 | |
| 物性表-ASTM(英文) | Technical Datasheet-ASTM(English) | 下载 |