ALTUGLAS™ R-Life V825T RED CR50 is an injection grade acrylic resins with applicability in automotive rear lighting applications.
It is made with 50% of recycled MMA monomer obtained by depolymerization of pre- and post-consumer waste streams according to ISO 14021 to lower the CO2 footprint, while meeting the same demanding requirements as its all-prime counterpart (outstanding optical properties, hardness, stiffness, UV stability, lightweight).
| 原厂资料 | 物性表(英文) | |||
| 供应市场 | 亚洲欧洲 | |||
| 产品特性 | 抗紫外线耐候性含回收料 | |||
| 应用产品 | 汽车尾灯罩 | |||
| 应用行业 | 汽车行业 | |||
| 颜色形状 | 粒状红色 | |||
| 成型方式 | 注塑 | |||
| 汽车材料 | 雷诺-日产(Renault-Nissan) EP10-1B | |||
| 回收料含量 | 50% 消费前/后回收(PIR/PCR) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 3 g/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.2~0.6 % | ASTM D 955 | |
吸水率 | 0.3 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 73 Mpa | ISO 527-2/5 | 23°C |
拉伸延伸率 | |||
断裂(brk) | 5 % | ISO 527-2/5 | 23°C |
弯曲模量 | 3300 Mpa | ISO 178 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 2 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 20 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 97 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 100 °C | ISO 75-2/A | Annealed |
维卡软化温度(Vicat) | 107 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 65 E-6/°C | ASTM D 696 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。