Polypropylene PPH 9099 is a polypropylene homopolymer with a Melt Flow Index of 27 g/10 min.
Polypropylene PPH 9099 is designed with a narrow molecular weight distribution and is intended for the extrusion of fine filaments in spunlaid nonwoven technologies (such as spunbond). It is characterised by excellent spinning properties and provides nonwovens with good mechanical properties and gas fading resistance.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 防烟熏褪色食品接触级均聚物 | |||
| 添加助剂 | 防烟熏褪色剂 | |||
| 成型方式 | 纺纱/丝 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 27 g/10min | ISO 1133 | |
堆积(视)密度 | 0.525 g/cm³ | ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 30 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
屈服(yld) | 10 % | ISO 527-2 | |
弯曲模量 | 1200 Mpa | ISO 178 | |
拉伸模量 | 1300 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 4 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 3.5 kJ/m² | ISO 180 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 92 R | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 95 °C | ISO 75 | 120°C per hour |
1.8 Mpa (264 psi)（18.6kg/cm²） | 52 °C | ISO 75 | 120°C per hour |
维卡软化温度(Vicat) | 148 °C | ISO 306 | 10N-50°C per hour |
维卡软化温度(Vicat) | 80 °C | ISO 306 | 50N-50°C per hour |
熔融温度(Tm) | 160~165 °C | ISO 3146 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。