Description
LI941-V has superior weatherability compared to general ASA
Key Features
High Heat Resistance, Non Painting, High Weatherability
Application
Bumper,Exterior ETC,Outside Mirror,Spoiler
| 原厂资料 | 物性表(英文)-ISO 物性表(英文)-ASTM | |||
| 产品特性 | 耐热免喷涂耐候性 | |||
| 成型方式 | 注塑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.08 g/cm³ | ISO 1183 | 23℃ |
密度 | 1.08 g/cm³ | ASTM D792 | 23℃ |
熔体质量流动速率(MFR) | |||
220℃/10 kg | 4 g/10 min | ISO 1133 | |
220℃/10 kg | 4 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.4~0.7 % | ASTM D 955 | 23℃, 3.2mm |
- | 0.4~0.7 % | ISO 294-4 | 23℃, 3.2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 45 Mpa | ASTM D638 | 3.2mm, 50mm/min |
屈服(yld) | 40 Mpa | ISO 527 | 50mm/min, 4mm |
拉伸延伸率 | |||
断裂(brk) | 15 % | ASTM D638 | 3.2mm, 50mm/min |
断裂(brk) | 15 % | ISO 527 | 50mm/min, 4mm |
弯曲强度 | |||
- | 70 Mpa | ASTM D790 | 6.4mm, 15mm/min |
- | 70 Mpa | ISO 178 | 2mm/min, 4mm |
弯曲模量 | 2200 Mpa | ASTM D790 | 6.4mm, 15mm/min |
弯曲模量 | 2000 Mpa | ISO 178 | 2mm/min, 4mm |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | 4mm |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 110 J/m | ASTM D256 | 3.2mm |
23℃ (73℉) | 110 J/m | ASTM D256 | 6.4mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 95 R | ASTM D785 | |
洛氏硬度R | 92 R | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 98 °C | ISO 75 | 4mm, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 94 °C | ASTM D648 | 6.4mm,Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 88 °C | ISO 75 | 4mm, Unannealed |
维卡软化温度(Vicat) | 98 °C | ASTM D1525 | 50N, 50℃/h |
维卡软化温度(Vicat) | 98 °C | ISO 306 | 50N, 50℃/h |