AKROMID® C3 GF 25 1 FR black (7246) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend, colored in black. Listed to UL 94 in black V0 @ 0,4 mm and all-colours V0 @ 0,8mm, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable for applications with high strength requirements in the automotive and E&E markets.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定阻燃无氯无红磷良好表面良好流动性填充增强 | |||
| 添加助剂 | 阻燃剂热稳定剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 25% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.37 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294-4 | |
横向(Across Flow) | 0.5~0.7 % | ISO 294-4 | |
吸湿率 | 1.8~2 % | ISO 1110 | 70°C, 62% r.H. |
螺旋流 | 480 mm | - | 2mm Thickness |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 95 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 137 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 5.5 % | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 3 % | ISO 527-2 | Dry, 5 mm/min |
弯曲强度 | |||
- | 160 Mpa | ISO 178 | Cond., 2 mm/min |
- | 225 Mpa | ISO 178 | Dry, 2 mm/min |
弯曲应变 | |||
断裂(brk) | 5 % | ISO 178 | Cond., 2 mm/min |
断裂(brk) | 3.5 % | ISO 178 | Dry, 2 mm/min |
弯曲模量 | 6000 Mpa | ISO 178 | Cond., 2 mm/min |
弯曲模量 | 8800 Mpa | ISO 178 | Dry, 2 mm/min |
拉伸模量 | 6300 Mpa | ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 9100 Mpa | ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 15 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | 11 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 75 kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | 66 kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 251 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 225 °C | ISO 75/A | |
8 Mpa (1160 psi)（81.6kg/cm²） | 168 °C | ISO 75/C | |
熔融温度(Tm) | 260 °C | ISO 11357-3 | DSC, 10K/min |
球压痕温度 | 210 °C | IEC 60695-10-2 | |
温度指数(TI)-拉伸强度 | |||
5000 h | 155 °C | IEC 60216 | 50% loss of tensile strength |
20000 h | 130 °C | IEC 60216 | 50% loss of tensile strength |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.4 mm | UL94 | |
V-0 | 0.8 mm | UL94 | |
V-0 | 1.6 mm | UL94 | |
V-0 | 3.2 mm | UL94 | |
5VA | 1.6 mm | UL94 | |
5VA | 3.2 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.4mm | 960 °C | IEC 60695-2-12 | |
0.8mm | 960 °C | IEC 60695-2-12 | |
1.6mm | 960 °C | IEC 60695-2-12 | |
3.2mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.4 mm | 750 °C | IEC 60695-2-13 | |
0.8mm | 750 °C | IEC 60695-2-13 | |
1.6mm | 750 °C | IEC 60695-2-13 | |
3.2mm | 750 °C | IEC 60695-2-13 | |
FMVSS | + pass | FMVSS 302 | > 1 mm Thickness |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相对漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | |
绝缘强度 | 12 kV/mm | IEC 60243 | 3 mm |
高电压电弧起痕速率(HVTR) | 0 PLC | UL 746A | |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 0,4mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 0,8mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 1,6mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 3,2mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 0,4mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 0,8mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 1,6mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 3,2mm |
斜面漏电起痕 | 1 kV | ASTM D2303 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。