AKROMID® C3 GF 25 1 FR black (7246) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend, colored in black. Listed to UL 94 in black V0 @ 0,4 mm and all-colours V0 @ 0,8mm, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable for applications with high strength requirements in the automotive and E&E markets.
| Original Document | Technical Datasheet(English) | |||
| Features | Heat StabilizedFlame RetardantCl- FreeNon Red PhosphorusGood SurfaceGood FlowFilled & Reinforced | |||
| Additive | Flame RetardantHeat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 25% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294-4 | |
Moisture /Humidity Absorption | ***~*** % | ISO 1110 | 70°C, 62% r.H. |
Spiral Flow | *** mm | - | 2mm Thickness |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Cond., 5 mm/min |
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 5 mm/min |
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Cond., 2 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Cond., 2 mm/min |
- | *** Mpa | ISO 178 | Dry, 2 mm/min |
Flexural Strain | |||
break | *** % | ISO 178 | Cond., 2 mm/min |
break | *** % | ISO 178 | Dry, 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
8 Mpa (1160 psi)（81.6kg/cm²） | *** °C | ISO 75/C | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
Ball Pressure Test | *** °C | IEC 60695-10-2 | |
Temperature index (TI)-Tensile Strength | |||
5000 h | *** °C | IEC 60216 | 50% loss of tensile strength |
20000 h | *** °C | IEC 60216 | 50% loss of tensile strength |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
0.4mm | *** °C | IEC 60695-2-12 | |
0.8mm | *** °C | IEC 60695-2-12 | |
1.6mm | *** °C | IEC 60695-2-12 | |
3.2mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.4mm | *** °C | IEC 60695-2-13 | |
0.8mm | *** °C | IEC 60695-2-13 | |
1.6mm | *** °C | IEC 60695-2-13 | |
3.2mm | *** °C | IEC 60695-2-13 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243 | 3 mm |
High Voltage Arc Tracking Rate(HVTR) | PLC | UL 746A | |
Hot Wire Ignition(HWI) | PLC | UL 746A | 0,4mm |
Hot Wire Ignition(HWI) | PLC | UL 746A | 0,8mm |
Hot Wire Ignition(HWI) | PLC | UL 746A | 1,6mm |
Hot Wire Ignition(HWI) | PLC | UL 746A | 3,2mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 0,4mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 0,8mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 1,6mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 3,2mm |
Inclined-Plane Tracking | *** kV | ASTM D2303 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.