SABIC® LDPE 2200H0 is a grade with a low melt flow range and contains no additives. This grade has a good draw down ability and very good optical properties.
Application
SABIC® LDPE 2200H0 is typically used for thin film applications combining high strength and good optical properties.
Film properties
Film properties have been measured at film of 50 μm with a BUR of 3. The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| 原厂资料 | 物性表(英文) | |||
| 成型方式 | 吹膜 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.922 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.33 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
摩擦系数 | 1 - | ASTM 1894 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 98 °C | ISO 306 | 10 N (VST/A) |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 8 % | ASTM D1003 | |
光泽度 | 57 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 11 Mpa | ISO 527-3 | TD |
断裂(brk) | 27 Mpa | ISO 527-3 | MD |
断裂(brk) | 22 Mpa | ISO 527-3 | TD |
拉伸延伸率 | |||
断裂(brk) | 200 % | ISO 527-3 | MD |
断裂(brk) | 500 % | ISO 527-3 | TD |
埃尔曼多夫撕裂 | 35 N/mm | ISO 6383-2 | MD |
埃尔曼多夫撕裂 | 40 N/mm | ISO 6383-2 | TD |
落锤冲击 | 30 J/mm | ASTM D4272 | |
弹性模量 | 190 MPa | ISO 527-3 | TD |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。