SABIC® LDPE 2200H0 is a grade with a low melt flow range and contains no additives. This grade has a good draw down ability and very good optical properties.
Application
SABIC® LDPE 2200H0 is typically used for thin film applications combining high strength and good optical properties.
Film properties
Film properties have been measured at film of 50 μm with a BUR of 3. The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| Original Document | Technical Datasheet(English) | |||
| Processing | Blown Film | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Coefficient of Friction | *** - | ASTM 1894 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 10 N (VST/A) |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | |
Gloss | *** - | ASTM D 2457 | 45° |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-3 | TD |
Break | *** Mpa | ISO 527-3 | MD |
Break | *** Mpa | ISO 527-3 | TD |
Tensile Elongation | |||
Break | *** % | ISO 527-3 | MD |
Break | *** % | ISO 527-3 | TD |
Elmondorf Tear | *** N/mm | ISO 6383-2 | MD |
Elmondorf Tear | *** N/mm | ISO 6383-2 | TD |
Dart Drop Impact | *** J/mm | ASTM D4272 | |
Elastic Modulus | *** MPa | ISO 527-3 | TD |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.