ULTEM PW2210 resin is an imporved flow 20% glass fiber reinforced amorphous polyetherimide (PEI) resin that is offering a high glass transition temperature (Tg) of 217°C. The material has global food contact compliance (FDA, CN, EC), potable water certifications: NSF 61, KTW-BWGL, EN16421. REG4, ACS, WRAS re-certifications are in progress. Features are excellent mechanical, and dimension properties up to high temperatures also under wet conditions. The material offers very good hydrolytic and chemical resistance for an amorphous material. The material is RoHS compliant. Certified colors are natural (transparent amber) and black.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热食品接触级饮用水级耐化学性良好流动性填充增强 | |||
| 颜色形状 | 粒状本色透明黑色褐色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | ACS(法国卫生认证)China GB13116-94(中国食品包装)DVGW W270(德国饮用水)EU 2011/10/EC (欧盟食品级)FDA(食品药品监督管理局)KTW(德国饮用水)NSF(美国卫生基金会食品认证)RoHS(欧盟电子电气设备中有害物质)WRAS(英国饮用水) | |||
| 增强填充 | 20% 玻纤 | |||
| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
|---|---|---|---|
密度/比重 | *** g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
360°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | ***~*** % | Internal | on Tensile Bar, flow |
吸水率 | *** % | ISO 62 | 23°C/sat |
吸湿率 | *** % | ISO 62 | 23°C / 50% RH |
磨耗 | *** mg/1000cy | Internal | Taber Abrasion, CS-17, 1 kg |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 | *** Mpa | ISO 527 | 1 mm/min |
拉伸强度 | |||
断裂(brk) | *** Mpa | ISO 527 | 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | *** % | ISO 527 | 5 mm/min |
弯曲模量 | *** Mpa | ISO 178 | 2 mm/min |
弯曲强度 | |||
断裂(brk) | *** Mpa | ISO 178 | 2 mm/min |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | *** kJ/m² | ISO 179/2C | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
球压硬度 | *** Mpa | ISO 2039-1 | H358/30 |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | *** °C | ISO 306/B50 | |
维卡软化温度(Vicat) | *** °C | ISO 306/A50 | |
维卡软化温度(Vicat) | *** °C | ISO 306/B120 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | *** E-6/°C | ISO 11359-2 | 23°C to 150°C, flow |
横向(Across Flow) | *** E-6/°C | ISO 11359-2 | 23°C to 150°C, xflow |
导热系数 | *** W/m-°C | ISO 8302 | |
球压痕温度 | *** °C | IEC 60695-10-2 | Pass |
| 燃烧性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
氧指数(LOI) | *** % | ISO 4589 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。