ULTEM PW2210 resin is an imporved flow 20% glass fiber reinforced amorphous polyetherimide (PEI) resin that is offering a high glass transition temperature (Tg) of 217°C. The material has global food contact compliance (FDA, CN, EC), potable water certifications: NSF 61, KTW-BWGL, EN16421. REG4, ACS, WRAS re-certifications are in progress. Features are excellent mechanical, and dimension properties up to high temperatures also under wet conditions. The material offers very good hydrolytic and chemical resistance for an amorphous material. The material is RoHS compliant. Certified colors are natural (transparent amber) and black.
| Original Document | Technical Datasheet(English) | |||
| Features | Heat ResistanceFood ContactDrinking Water ContactChemical ResistanceGood FlowFilled & Reinforced | |||
| Appearance | Pellets/GranulesNatural ColorClear/TransparentBlackBrown | |||
| Processing | Injection | |||
| Compliance | ACSChina GB13116-94DVGW W270EU 2011/10/ECFDAKTWNSFRoHSWRAS | |||
| Reinforced | 20% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
360°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | on Tensile Bar, flow |
Water Absorption | *** % | ISO 62 | 23°C/sat |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% RH |
Abrasion resistance | *** mg/1000cy | Internal | Taber Abrasion, CS-17, 1 kg |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
Break | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/2C | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | H358/30 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B120 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359-2 | 23°C to 150°C, flow |
Across Flow | *** E-6/°C | ISO 11359-2 | 23°C to 150°C, xflow |
Thermal Conductivity | *** W/m-°C | ISO 8302 | |
Ball Pressure Test | *** °C | IEC 60695-10-2 | Pass |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Oxygen Index | *** % | ISO 4589 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.