POKETONE Polymer M33AG6A is a 30 percent short glass-fiber-reinforced high-flow injection moulding grade with mechanical properties that classify it as an engineering thermoplastic. This grade shows a unique balance of toughness and high modulus combined with good creep performance, strength and elevated temperature performance.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高流动填充增强 | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.47 g/cm³ | ASTM D792 | |
比重 | 1.47 - | ISO 1183 | |
熔体体积流动速率(MVR) | |||
240℃/2.16 kg | 13 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
240℃/2.16kg | 14 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.1 % | ASTM D 955 | 2mm |
纵向(Flow) | 0.2 % | ASTM D 955 | 3mm |
横向(Across Flow) | 0.9 % | ASTM D 955 | 2mm |
横向(Across Flow) | 1.1 % | ASTM D 955 | 3mm |
吸水率 | 1.7 % | ASTM D570 | |
吸水率 | 1.7 % | ISO 62 | |
吸湿率 | 0.4 % | ISO 62 | |
吸湿率 | 0.4 % | ASTM D 570 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 140 Mpa | ASTM D638 | |
屈服(yld) | 140 Mpa | ISO 527-1 | |
拉伸延伸率 | |||
断裂(brk) | 3.8 % | ASTM D638 | |
断裂(brk) | 3.8 % | ISO 527-1 | |
弯曲强度 | |||
- | 190 Mpa | ASTM D790 | |
- | 185 Mpa | ISO 178 | |
弯曲模量 | 6700 Mpa | ASTM D790 | |
弯曲模量 | 6150 Mpa | ISO 178 | |
拉伸模量 | 7700 Mpa | ASTM D638 | |
拉伸模量 | 7500 Mpa | ISO 527-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 13 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 120 J/m | ASTM D256 | |
23℃ (73℉) | 13 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 104 kJ/m² | ISO 180/1U | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 113 R | ASTM D785 | |
邵氏硬度 D | 81 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 215 °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | 215 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ISO 75 | |
维卡软化温度(Vicat) | 210 °C | ASTM D1525 | |
维卡软化温度(Vicat) | 210 °C | ISO 306 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 28 E-6/°C | ASTM E831 | 25℃ to 55℃ |
横向(Across Flow) | 97 E-6/°C | ASTM E831 | 25℃ to 55℃ |
熔融温度(Tm) | 222 °C | ASTM D3418 | |
熔融温度(Tm) | 222 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.8 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+14 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+17 Ohm | ASTM D257 | |
介电常数(DK) | |||
60 Hz | 6.3 - | ASTM D 150 | |
耗散因数(DF) | |||
60 Hz | 110 E-4 | ASTM D 150 | |
相对漏电起痕指数(CTI ) | |||
- | 0 PLC | UL 746A | 3.2mm |
绝缘强度 | 22 kV/mm | ASTM D149 | 2mm |
绝缘强度 | 17 kV/mm | ASTM D149 | 3mm |
高电压电弧起痕速率(HVTR) | 1 PLC | UL 746A | 3.2mm |
热线圈起燃性(HWI) | 4 PLC | UL 746A | 0.8mm |
热线圈起燃性(HWI) | 2 PLC | UL 746A | 1.6mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 3.2mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A |