POKETONE Polymer M33AG6A is a 30 percent short glass-fiber-reinforced high-flow injection moulding grade with mechanical properties that classify it as an engineering thermoplastic. This grade shows a unique balance of toughness and high modulus combined with good creep performance, strength and elevated temperature performance.
| Original Document | Technical Datasheet(English) | |||
| Features | High FlowFilled & Reinforced | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
240℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
240℃/2.16kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | *** % | ASTM D955 | 2mm |
Flow | *** % | ASTM D955 | 3mm |
Across Flow | *** % | ASTM D955 | 2mm |
Across Flow | *** % | ASTM D955 | 3mm |
Water Absorption | *** % | ASTM D570 | |
Water Absorption | *** % | ISO 62 | |
Moisture /Humidity Absorption | *** % | ISO 62 | |
Moisture /Humidity Absorption | *** % | ASTM D 570 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | |
Tensile Modulus | *** Mpa | ISO 527-1 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Yield | *** Mpa | ISO 527-1 | |
Tensile Elongation | |||
Break | *** % | ASTM D638 | |
Break | *** % | ISO 527-1 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1U | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
Shore D hardness | *** D | ISO 868 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | 25℃ to 55℃ |
Across Flow | *** E-6/°C | ASTM E831 | 25℃ to 55℃ |
Melt Temperature(Tm) | *** °C | ASTM D3418 | |
Melt Temperature(Tm) | *** °C | ISO 11357 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Surface Resistivity | *** Ohm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
60 Hz | *** - | ASTM D 150 | |
Dissipation Factor | |||
60 Hz | *** E-4 | ASTM D 150 | |
Comparative Tracking Index (CTI) | |||
- | PLC | UL 746A | 3.2mm |
Dielectric Strength | *** kV/mm | ASTM D149 | 2mm |
Dielectric Strength | *** kV/mm | ASTM D149 | 3mm |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746A | 3.2mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746A | 0.8mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746A | 1.6mm |
Hot Wire Ignition(HWI) | PLC | UL 746A | 3.2mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.