A fluororesin suitable for compound with additives such as carbon.
Introduction
- POLYFLON M-18F is a polytetrafluoroethylene virgin granular fine cut resin.
- Compressing the powder and sintering are a general method for use due to its high melt viscosity.
- Suitable for compound material with additives such as carbon.
| 原厂资料 | 物性表(英文) | |||
| 颜色形状 | 粉末状 | |||
| 成型方式 | 烧结 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 2.16 g/cm³ | ASTM D4894 | |
收缩率 | |||
- | 3.7 % | Internal | 50Φ × 50h |
粒子大小 | 25 micrometer | ASTM D4894 | Average |
堆积(视)密度 | 0.33 g/cm³ | ASTM D4894 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 58 Mpa | ASTM D4894 | |
拉伸延伸率 | |||
- | 440 % | ASTM D4894 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 345 °C | ASTM D4894 | Initial |
熔融温度(Tm) | 327 °C | ASTM D4894 | Second |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。