Epocast® 1635-A/B syntactic compound is a two-component, high-performance material designed for refilling mis-drilled holes in composite parts. This aluminum filled, high-viscosity system exhibits outstanding compressive strength and dynamic fatigue resistance under load at elevated temperature. This product is qualified to BMS 5-28, Type 31.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐疲劳耐热高粘度填充增强 | |||
| 颜色形状 | 灰色 | |||
| 成型方式 | 挤出 | |||
| 增强填充 | 铝 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.8 g/cm³ | ASTM D 1622 | Part A |
密度 | 1.7 g/cm³ | ASTM D 1622 | Part B |
密度 | 1.8 g/cm³ | ASTM D 1622 | System |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
剪切强度 | 10.34 Mpa | ASTM D1002 | Tensile lap shear, 2.5 hours@93ºC |
抗压强度 | 82.74 Mpa | ASTM D 695 | 177ºC after 2.5 hours@93ºC |
抗压强度 | 82.74 Mpa | ASTM D 695 | 177ºC after 7days@25ºC |
抗压强度 | 172.4 Mpa | ASTM D 695 | 25ºC after 2.5 hours@93ºC |
抗压强度 | 103.4 Mpa | ASTM D 695 | 25ºC after 7days@25ºC |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。