Epocast® 1635-A/B syntactic compound is a two-component, high-performance material designed for refilling mis-drilled holes in composite parts. This aluminum filled, high-viscosity system exhibits outstanding compressive strength and dynamic fatigue resistance under load at elevated temperature. This product is qualified to BMS 5-28, Type 31.
| Original Document | Technical Datasheet(English) | |||
| Features | Fatigue ResistantHeat ResistanceHigh ViscosityFilled & Reinforced | |||
| Appearance | Gray Color | |||
| Processing | Extrusion | |||
| Reinforced | Aluminium | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1622 | Part A |
Density/Specific Gravity | *** g/cm³ | ASTM D 1622 | Part B |
Density/Specific Gravity | *** g/cm³ | ASTM D 1622 | System |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shear Strength | *** Mpa | ASTM D1002 | Tensile lap shear, 2.5 hours@93ºC |
Compressive Strength | *** Mpa | ASTM D 695 | 177ºC after 2.5 hours@93ºC |
Compressive Strength | *** Mpa | ASTM D 695 | 177ºC after 7days@25ºC |
Compressive Strength | *** Mpa | ASTM D 695 | 25ºC after 2.5 hours@93ºC |
Compressive Strength | *** Mpa | ASTM D 695 | 25ºC after 7days@25ºC |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.