Enable™ 2010 resins are ethylene 1-hexene copolymers. Enable™ performance polymer resins offer an outstanding balance between processing and film properties, including tensile, impact and puncture. TnPP is not intentionally added to Enable™ 2010 resins.
| 原厂资料 | 物性表(英文) 物性表(中文) | |||
| 添加助剂 | 热稳定剂加工助剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 流延薄膜吹膜吹灌封(BFS) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.92 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 106 °C | Internal | |
熔融温度(Tm) | 114 °C | Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 7 % | ASTM D1003 | |
光泽度 | 62 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 9.6 Mpa | ASTM D 882 | MD |
屈服(yld) | 10 Mpa | ASTM D 882 | TD |
断裂(brk) | 50 Mpa | ASTM D 882 | MD |
断裂(brk) | 50 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 510 % | ASTM D 882 | MD |
断裂(brk) | 720 % | ASTM D 882 | TD |
穿透强度 | 47 N | Internal | |
耐穿透性 | 3.2 J | Internal | |
埃尔曼多夫撕裂 | 130 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 550 g | ASTM D 1922 | TD |
割线模量 | 200 Mpa | ASTM D 882 | MD, 1% Secant |
割线模量 | 230 Mpa | ASTM D 882 | TD, 1% Secant |
落锤冲击 | 180 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。