| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
密度/比重 |
*** g/cm³
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
*** g/10min | ASTM D1238 | |
300°C/3.8 kg |
*** g/10 min | ASTM D 1238 | |
300°C/5.0 kg |
*** g/10 min | ASTM D 1238 | |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 |
*** Mpa
| ASTM D638 | 23°C, 3.11 mm, Injection Molded |
拉伸强度 | | | |
断裂(brk) |
*** Mpa | ASTM D638 | 23°C, 3.11 mm, Injection Molded |
拉伸延伸率 | | | |
断裂(brk) |
*** % | ASTM D638 | 23°C, 3.11 mm, Injection Molded |
弯曲模量 |
*** Mpa
| ASTM D790 | 1% Secant |
弯曲强度 | | | |
屈服(yld) |
*** Mpa | ASTM D790 | |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
*** J/m | ASTM D256 | 3.07 mm |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
*** J/m | ASTM D256 | 3.08 mm |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ASTM D648 | Unannealed, 12.6 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | Unannealed, 12.6 mm |
维卡软化温度(Vicat) |
*** °C
| ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) |
*** °C
| ASTM D1525 | Rate B (120°C/h), Loading 2 (50 N) |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
*** E-6 cm/cm/℃ | ASTM D 696 | -20 to 130°C |
横向(Across Flow) |
*** E-6 cm/cm/℃ | ASTM D 696 | -20 to 130°C |
| 燃烧性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
FMVSS |
*** mm/min
| FMVSS 302 | |
燃烧速率 |
*** mm/min
| ISO 3795 | |