32% Glass Fiber Reinforced Polycarbonate
| Original Document | Technical Datasheet-ASTM(English) | |||
| Features | Filled & Reinforced | |||
| Appearance | Black | |||
| Processing | InjectionExtrusion | |||
| Reinforced | 32% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ASTM D1238 | |
300°C/3.8 kg | *** g/10 min | ASTM D 1238 | |
300°C/5.0 kg | *** g/10 min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 23°C, 3.11 mm, Injection Molded |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | 23°C, 3.11 mm, Injection Molded |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 23°C, 3.11 mm, Injection Molded |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | 3.07 mm |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | 3.08 mm |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 12.6 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 12.6 mm |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B (120°C/h), Loading 2 (50 N) |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM D 696 | -20 to 130°C |
Across Flow | *** E-6 cm/cm/℃ | ASTM D 696 | -20 to 130°C |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
FMVSS | *** mm/min | FMVSS 302 | |
Burning Rate | *** mm/min | ISO 3795 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.