| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
密度/比重 |
*** g/cm³
| ISO 1183 | |
密度/比重 |
*** g/cm³
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
*** % | ASTM D955 | 1.59 mm |
纵向(Flow) |
*** % | ASTM D955 | 3.18 mm |
纵向(Flow) |
*** % | ISO 294-4 | 1.59 mm |
纵向(Flow) |
*** % | ISO 294-4 | 3.18 mm |
横向(Across Flow) |
*** % | ASTM D955 | 1.59 mm |
横向(Across Flow) |
*** % | ASTM D955 | 3.18 mm |
横向(Across Flow) |
*** % | ISO 294-4 | 1.59 mm |
横向(Across Flow) |
*** % | ISO 294-4 | 3.18 mm |
粘度 |
*** Pa-s
| ASTM D 3835 | Melt Viscosity (190°C, 300 sec^-1) |
磨耗 |
*** mg/1000cy
| ASTM D 1044 | 1.0E+6 g, CS-17 Wheel |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
*** Mpa | ASTM D 412 | 23°C |
屈服(yld) |
*** Mpa | ISO 37 | 23°C |
100%延伸率时 |
*** Mpa | ASTM D 412 | |
100%延伸率时 |
*** Mpa | ISO 37 | 23°C |
拉伸延伸率 | | | |
断裂(brk) |
*** % | ASTM D 412 | |
断裂(brk) |
*** % | ISO 37 | 23°C |
撕裂强度 |
*** kN/m
| ASTM D 624 | 24°C, Die C |
压缩永久形变 |
*** %
| ASTM D 395 | 100°C, 22 hr |
压缩永久形变 |
*** %
| ASTM D 395 | 24°C, 22 hr |
压缩永久形变 |
*** %
| ASTM D 395 | 70°C, 22 hr |
压缩永久形变 |
*** %
| ISO 815 | 100°C, 22 hr |
压缩永久形变 |
*** %
| ISO 815 | 24°C, 22 hr |
压缩永久形变 |
*** %
| ISO 815 | 70°C, 22 hr |
拉伸形变 |
*** %
| ASTM D 412 | 100% Strain |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
脆化温度 |
*** °C
| ASTM D 746 | |
脆化温度 |
*** °C
| ISO 812 | |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
邵氏硬度 A |
*** A
| ASTM D 2240 | 5 sec |
邵氏硬度 A |
*** A
| ISO 868 | 5 sec |
| 老化性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸强度(热老化) |
*** %
| ISO 188 | Change in Air, 100°C, 168 hr |
拉伸强度(热老化) |
*** %
| ISO 188 | Change in Air, 70°C, 168 hr |
拉伸强度(热老化) |
*** %
| ASTM D573 | Change in Air, 100°C, 168 hr |
拉伸强度(热老化) |
*** %
| ASTM D573 | Change in Air, 70°C, 168 hr |
延伸率(热老化) |
*** %
| ASTM D573 | Change in Ultimate Elongation in Air, 100°C, 168 hr |
延伸率(热老化) |
*** %
| ASTM D573 | Change in Ultimate Elongation in Air, 70°C, 168 hr |
体积变化 |
*** %
| ISO 1817 | 100°C, 168 hr, in ASTM #1 Oil |
体积变化 |
*** %
| ISO 1817 | 100°C, 168 hr, in IRM 903 Oil |
体积变化 |
*** %
| ISO 1817 | 100°C, 168 hr, in Wate |
体积变化 |
*** %
| ISO 1817 | 24°C, 168 hr, in Reference Fuel B |
体积变化 |
*** %
| ASTM D471 | 100°C, 168 hr, in ASTM #1 Oil |
体积变化 |
*** %
| ASTM D471 | 100°C, 168 hr, in IRM 903 Oil |
体积变化 |
*** %
| ASTM D471 | 100°C, 168 hr, in Wate |
体积变化 |
*** %
| ASTM D471 | 24°C, 168 hr, in Reference Fuel B |
拉伸模量 |
*** %
| ASTM D573 | Change in Air, 100°C, 168 hr |
拉伸模量 |
*** %
| ASTM D573 | Change in Air, 70°C, 168 hr |