PPA, 30% glass fiber reinforced V0, halogens free, complying with RoHS and WEEE.
FRIANYL XT4 compounds are designed for electrical and electronic applications requiring a maximum service temperature higher than that of standard polyamides. The most relevant characteristics are the following: High stiffness and strength at elevated temperatures V-0 according to the UL 94 flammability standard Excellent creep behavior Small influence on mechanical properties after moisture uptake Good dimensional stability Low warpage
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性耐热阻燃无卤尺寸稳定低翘曲抗蠕变填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质)WEEE(欧盟报废电子气设备) | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.43 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.3 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1 % | ISO 294-4, 2577 | |
吸水率 | 3 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 145 Mpa | ISO 527-2/1A | Dry, 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 1.6 % | ISO 527-2/1A | Dry, 5mm/min |
弯曲强度 | |||
断裂(brk) | 35 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 240 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 12500 Mpa | ISO 527-2/1A | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 8 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 32 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 35 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 295 °C | ISO 75-1/-2 | Dry |
熔融温度(Tm) | 325 °C | ISO 11357-1/-3 | |
连续使用温度 | |||
- | 140 °C | IEC 60216-1 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.4 mm | UL94 | Dry |
V-0 | 0.8 mm | UL94 | Dry |
V-0 | 1.6 mm | UL94 | Dry |
V-0 | 3.2 mm | UL94 | Dry |
灼热丝可燃性指数(GWFI) | |||
0.8mm | 960 °C | IEC 60695-2-12 | |
3.2mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.8mm | 800 °C | IEC 60695-2-13 | |
3.2mm | 875 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+10 Ohm-m | IEC 60093 | Dry |
表面电阻率 | 1.0E+11 Ohm | IEC 60093 | Dry |
相对漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | Dry |
绝缘强度 | 35 kV/mm | IEC 60243-1 | Dry |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。