PPA, 30% glass fiber reinforced V0, halogens free, complying with RoHS and WEEE.
FRIANYL XT4 compounds are designed for electrical and electronic applications requiring a maximum service temperature higher than that of standard polyamides. The most relevant characteristics are the following: High stiffness and strength at elevated temperatures V-0 according to the UL 94 flammability standard Excellent creep behavior Small influence on mechanical properties after moisture uptake Good dimensional stability Low warpage
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat ResistanceFlame RetardantHalogen FreeDimensional StabilityLow WarpageCreep ResistantFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Appearance | Pellets/GranulesBlack | |||
| Compliance | RoHSWEEE(EU 2002/96/EC) | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | |
Across Flow | *** % | ISO 294-4, 2577 | |
Water Absorption | *** % | ISO 62 | 23°C-sat |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C/50%RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | Dry |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A | Dry, 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A | Dry, 5mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 23°C |
Flexural Strength | |||
Break | *** Mpa | ISO 178 | Dry, 23°C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Dry |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | |
Continuous Use Temperature | |||
Long term | *** °C | IEC 60216-1 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | Dry |
V-0 | *** mm | UL94 | Dry |
V-0 | *** mm | UL94 | Dry |
V-0 | *** mm | UL94 | Dry |
Glow Wire Flammability Index(GWFI) | |||
0.8mm | *** °C | IEC 60695-2-12 | |
3.2mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.8mm | *** °C | IEC 60695-2-13 | |
3.2mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | Dry |
Surface Resistivity | *** Ohm | IEC 60093 | Dry |
Comparative Tracking Index (CTI) | |||
- | *** - | IEC 60112 | Dry |
Dielectric Strength | *** kV/mm | IEC 60243-1 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.