Glass fibre reinforced thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding impact strength, high stiffness whilst maintaining good elongation, low coefficiant of expansion similar to Aluminium, low shrinkage, good paintability.
Typical applications
Automotive body and panels and structural door trim parts, under body sealants, technical mouldings e.g. plugs, ski tips.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性高冲击易涂装填充增强 | |||
| 应用产品 | 车门内饰板车身面板插头/塞子密封件滑雪板板头 | |||
| 颜色形状 | 本色 | |||
| 成型方式 | 注塑 | |||
| 曲线坐标点 | 动态剪切模量-温度应力-应变 (等时的) 23°C蠕变模量-时间 23°C | |||
| 增强填充 | 20% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.38 g/cm³ | ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 80 Mpa | ISO 527 | strain rate at 50mm/min |
拉伸延伸率 | |||
断裂(brk) | 10 % | ISO 527 | strain rate at 50mm/min |
拉伸模量 | 2800 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179 | |
23℃ (73℉) | 30 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 70 kJ/m² | ISO 179 | |
23℃ (73℉) | 120 kJ/m² | ISO 179 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 73 D | ISO 7619 | 3s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 155 °C | ISO 75-2/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 120 °C | ISO 75-2/A | |
线性膨胀系数(CLTE) | |||
- | 20 E-6/K | DIN 53752 | between 23°C and 80°C |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。