Glass fibre reinforced thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding impact strength, high stiffness whilst maintaining good elongation, low coefficiant of expansion similar to Aluminium, low shrinkage, good paintability.
Typical applications
Automotive body and panels and structural door trim parts, under body sealants, technical mouldings e.g. plugs, ski tips.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHigh ImpactGood PaintablilityFilled & Reinforced | |||
| Applications | Door TrimAutomotive Body PanelsPlugsSealsSki Tips | |||
| Appearance | Natural Color | |||
| Processing | Injection | |||
| Technical Notes | Modulus of elasticity-TemperatureStress-strainCoefficient of thermal expansion α-TemperatureHeat Deflection temperature(HDT)Vicat softening temperature (VST)Stress-strain (isochronous)(creep) | |||
| Diagrams | Dynamic Shear modulus-temperatureStress-strain (isochronous)(Creep) 23°CCreep modulus-time 23°C | |||
| Reinforced | 20% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | |
Tensile Strength | |||
- | *** Mpa | ISO 527 | strain rate at 50mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | strain rate at 50mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | |
23℃ (73℉) | *** kJ/m² | ISO 179 | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | |
23℃ (73℉) | *** kJ/m² | ISO 179 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 7619 | 3s |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | DIN 53752 | between 23°C and 80°C |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.