LNP COLORCOMP J1000AE is an unfilled Polyethersulfone. Added feature of this grade is: Easy Molding.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantEasy processing | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | ***~*** % | ASTM D955 | flow, 24 hrs |
Moisture /Humidity Absorption | *** % | ASTM D 570 | 50% RH, 24 hrs |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 5 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
Break | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM D 696 | -30°C to 30°C, flow |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Dissipation Factor | |||
50/60 Hz | *** E-4 | ASTM D 150 | |
1 kHz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | ASTM D150 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.