PPE+PS blend. 30% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. RTI 110/105/110. Dielectric strength. Dimensional stability. Suitable for E/E applications.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantCl- FreeBr- FreeDimensional StabilityFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | 3.2 mm |
Water Absorption | *** % | ASTM D570 | 24 hours |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 100 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 100 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell L | *** L | ASTM D 785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 95°C |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-1 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589 | LOI |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Dielectric Constant(Permittivity) | |||
50/60 Hz | *** - | ASTM D150 | |
Dissipation Factor | |||
50/60 Hz | *** E-4 | ASTM D 150 | |
Comparative Tracking Index (CTI)-PLC | |||
PLC3 (175 - 249 V) | *** - | UL 746A | |
Dielectric Strength | *** kV/mm | ASTM D149 | in oil, 3.2 mm 20.8 kV/ |
Arc Resistance-PLC | |||
PLC6 (60 -119 s) | *** - | ASTM D495 | |
High Voltage Arc Tracking Rate(HVTR)-PLC | |||
PLC4 (> 150 mm/min) | *** - | UL 746A | |
Hot Wire Ignition(HWI)-PLC | |||
PLC0 (≥ 120 s) | *** mm | UL 746A | |
High Ampere Arc Ignition(HAI)-PLC | |||
PLC2 (30 -59 times) | *** mm | UL 746A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.