PPE+PS blend. 10% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. RTI 110/105/110. Dielectric strength. Dimensional stability. Suitable for E/E applications.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantCl- FreeBr- FreeDimensional StabilityFilled & Reinforced | |||
| Reinforced | 10% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 3.2 mm |
Water Absorption | *** % | ASTM D570 | 24 hours |
Water Absorption | *** % | ASTM D570 | equilibrium, 23C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | Type I,5 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I,5 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
Break | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell L | *** L | ASTM D 785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B/50 |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-1 | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589 | LOI |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
50/60 Hz | *** - | ASTM D150 | |
1MHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
50/60 Hz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | ASTM D150 | |
Comparative Tracking Index (CTI)-PLC | |||
PLC2 (250-399V) | *** - | UL 746A | |
High Voltage Arc Tracking Rate(HVTR)-PLC | |||
PLC4 (> 150mm/min) | *** - | UL 746A | |
Hot Wire Ignition(HWI)-PLC | |||
PLC1 (60-119s) | *** mm | UL 746A | |
High Ampere Arc Ignition(HAI)-PLC | |||
PLC2 (30-59 times) | *** mm | UL 746A | surface |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.