VALOX V3900WX is an unreinforced, UV stabilized, weatherable, impact modified flame retardant Polybutylene Terephthalate/Polycarbonate (PBT) injection moldable grade. It has excellent chemical resistance and a UL94V0@1.5mm and 5VA@3.0mm flame rating. This is an excellent candidate for a wide variety of applications including outdoor enclosures requiring UL746C F1 weatherability performance.
| 原厂资料 | 物性表(英文) | |||
| 供应市场 | 亚洲 | |||
| 产品特性 | 高冲击阻燃抗紫外线耐候性耐化学性 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.3 g/cm³ | ISO 1183 | |
比重 | 1.3 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
265℃/2.16 kg | 11 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
266℃/5.0 kg | 35 g/10 min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.7~1 % | Internal | flow, 3.2 mm |
吸水率 | 0.1 % | ISO 62 | 23°C/sat |
吸湿率 | 0.03 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 53 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 51 Mpa | ISO 527 | 50 mm/min |
屈服(yld) | 48 Mpa | Internal | |
断裂(brk) | 40 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 43 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 4 % | ISO 527 | 50 mm/min |
断裂(brk) | 250 % | ASTM D638 | |
断裂(brk) | 50 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 42 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 80 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 73 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2200 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2130 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2200 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2090 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 52 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 110 J/m | ASTM D256 | |
-30℃ (-22℉) | 8 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 800 J/m | ASTM D256 | |
23℃ (73℉) | 45 kJ/m² | ISO 180/1A | 80*10*4 |
仪器化落镖冲击能量 | |||
-40℃ (-40℉)总能量 | 50 J | ASTM D3763 | |
23℃ (73℉)总能量 | 50 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 119 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 75 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 96 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 77 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 105 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 123 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 121 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击Imp,- | 120 °C | UL 746B | |
电气Elec,- | 120 °C | UL 746B | |
强度Str,- | 120 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 88.4 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 88.4 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 89.7 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 89.7 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
球压痕温度 | 75 °C | IEC 60695-10-2 | Pass |
球压痕温度 | 125 °C | IEC 60695-10-2 | Pass |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
5VA | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | passes at |
3mm | 960 °C | IEC 60695-2-12 | passes at, by VDE |
灼热丝点燃温度(GWIT) | |||
1.0mm | 825 °C | IEC 60695-2-13 | |
3.0mm | 725 °C | IEC 60695-2-13 | by VDE |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C |