PBT+PC, 20 % glass fibers, injection molding, low tendency to warp, improved surface finish, improved laser-transparency, NIR-laser transparent coloring (black)
ISO Shortname: ISO 20028-PBT+PC,GF20,GHMR,09-050
| Original Document | Technical Datasheet-ISO(English) | |||
| Status | Business Restructured | |||
| Features | Good SurfaceLow WarpageFilled & Reinforced | |||
| Appearance | Black | |||
| Processing | Injection | |||
| Reinforced | 20% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
260°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 2577 | 150x105x3;110℃;1h |
Flow | *** % | ISO 2577 | 150x105x3;260℃/MT 80℃;600 bar |
Across Flow | *** % | ISO 2577 | 150x105x3;110℃;1h |
Across Flow | *** % | ISO 2577 | 150x105x3;260℃/MT 80℃;600 bar |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
Water Absorption | *** % | ISO 62 | Saturation, 23°C |
Viscosity | *** Pa-s | Internal | 165 1/s; 260 °C |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | 5mm/min |
Flexural Modulus | *** Mpa | ISO 178/1A | 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178/A | 2mm/min |
Flexural Strain | |||
- | *** % | ISO 178/A | 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 120℃/h |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10℃/min |
Processing Temperature | *** °C | - | Injection molding |
Mould temperature | *** °C | - | Injection molding |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.