PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, improved laser-transparency, NIR-laser transparent coloring (black)
ISO Shortname: ISO 20028-PBT+PC,,GHLMPR,11-020
| Original Document | Technical Datasheet-ISO(English) | |||
| Status | Business Restructured | |||
| Features | High ImpactLow Warpage | |||
| Appearance | Black | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
270°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 60x60x2; 250℃/WZ 70℃;600 bar |
Across Flow | *** % | ISO 294-4 | 60x60x2; 250℃/WZ 70℃;600 bar |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50mm/min |
Flexural Modulus | *** Mpa | ISO 178/A | 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178/A | 2mm/min |
3.5% strain | *** Mpa | ISO 178/A | 2mm/min |
Flexural Strain | |||
- | *** % | ISO 178/A | 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 120℃/h |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10℃/min |
Processing Temperature | *** °C | - | Injection molding |
Mould temperature | *** °C | - | Injection molding |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.