PBT+ASA, 30 % glass fibers, injection molding, flame retardant, low tendency to warp
ISO Shortname: ISO 20028-PBT+ASA,GF30,GFMR,09-110; ISO1043-4 FR(17)
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Flame RetardantLow WarpageFilled & Reinforced | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
260°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 60x60x2; 120℃; 4 h |
Flow | *** % | ISO 294-4 | 60x60x2; 250℃/WZ 80℃;600 bar |
Across Flow | *** % | ISO 294-4 | 60x60x2; 120℃; 4 h |
Across Flow | *** % | ISO 294-4 | 60x60x2; 250℃/WZ 80℃;600 bar |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | 5mm/min |
Flexural Modulus | *** Mpa | ISO 178/1A | 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178/A | 2mm/min |
Flexural Strain | |||
- | *** % | ISO 178/A | 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 120℃/h |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10℃/min |
Ball Pressure Test | *** °C | IEC 60695-10-2 | |
Processing Temperature | *** °C | - | Injection molding |
Mould temperature | *** °C | - | Injection molding |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589 | Method A |
Glow Wire Flammability Index(GWFI) | |||
0.75mm | *** °C | IEC 60695-2-12 | |
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.75mm | *** °C | IEC 60695-2-13 | |
1.5mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Solution A | *** PLC | UL 746 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | 1mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.