| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 1183 | |
Mold Shrinkage | | | |
Flow |
*** % | ISO 2577 | 150x105x3;120℃;4 h |
Flow |
*** % | ISO 2577 | 150x105x3;280℃/MT 80℃;500 bar |
Flow |
*** % | ISO 2577 | 60x60x2; 120℃; 4 h |
Flow |
*** % | ISO 2577 | 60x60x2; 280℃/MT 80℃;600 bar |
Across Flow |
*** % | ISO 2577 | 150x105x3;120℃;4 h |
Across Flow |
*** % | ISO 2577 | 150x105x3;280℃/MT 80℃;500 bar |
Across Flow |
*** % | ISO 2577 | 60x60x2; 120℃; 4 h |
Across Flow |
*** % | ISO 2577 | 60x60x2; 280℃/MT 80℃;600 bar |
Water Absorption |
*** %
| ISO 62 | Equilibrium, 23°C, 50% RH |
Water Absorption |
*** %
| ISO 62 | Saturation, 23°C |
Bulk(Apparent ) Density |
*** g/cm³
| ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus |
*** Mpa
| ISO 527-1/-2 | Dry,1mm/min |
Tensile Modulus |
*** Mpa
| ISO 527-1/-2 | cond. ,1mm/min |
Tensile Strength | | | |
Break |
*** Mpa | ISO 527-1/-2 | Dry,5mm/min |
Break |
*** Mpa | ISO 527-1/-2 | cond. ,5mm/min |
Tensile Elongation | | | |
Break |
*** % | ISO 527-1/-2 | Dry,5mm/min |
Break |
*** % | ISO 527-1/-2 | cond. ,5mm/min |
Flexural Modulus |
*** Mpa
| ISO 178/A | Dry,2mm/min |
Flexural Modulus |
*** Mpa
| ISO 178/A | cond. ,2mm/min |
Flexural Strength | | | |
- |
*** Mpa | ISO 178/A | Dry,2mm/min |
- |
*** Mpa | ISO 178/A | cond. ,2mm/min |
3.5% strain |
*** Mpa | ISO 178/A | Dry,2mm/min |
3.5% strain |
*** Mpa | ISO 178/A | cond. ,2mm/min |
Flexural Strain | | | |
- |
*** % | ISO 178/A | Dry,2mm/min |
- |
*** % | ISO 178/A | cond. ,2mm/min |
Tensile Creep Modulus | | | |
1h |
*** Mpa | ISO 899-1 | cond. |
1000h |
*** Mpa | ISO 899-1 | cond. |
Puncture | | | |
Force |
*** N | ISO 6603-2 | Dry, -30℃ |
Force |
*** N | ISO 6603-2 | Dry, 23℃ |
Force |
*** N | ISO 6603-2 | cond. ,23℃ |
Force |
*** N | ISO 6603-2 | cond. ,23℃ |
Energy |
*** J | ISO 6603-2 | Dry, -30℃ |
Energy |
*** J | ISO 6603-2 | Dry, 23℃ |
Energy |
*** J | ISO 6603-2 | cond. ,-30℃ |
Energy |
*** J | ISO 6603-2 | cond. ,-30℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | | | |
-30℃ (-22℉) |
*** kJ/m² | ISO 179/1eA | Dry |
-30℃ (-22℉) |
*** kJ/m² | ISO 179/1eA | cond. |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | cond. |
Charpy Unnotched Impact Strengh | | | |
-30℃ (-22℉) |
*** kJ/m² | ISO 179/1eU | Dry |
-30℃ (-22℉) |
*** kJ/m² | ISO 179/1eU | cond. |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eU | cond. |
Izod Notched Impact Strengh | | | |
-30℃ (-22℉) |
*** kJ/m² | ISO 180/1A | Dry |
-30℃ (-22℉) |
*** kJ/m² | ISO 180/1A | cond. |
23℃ (73℉) |
*** kJ/m² | ISO 180/1A | Dry |
23℃ (73℉) |
*** kJ/m² | ISO 180/1A | cond. |
Izod Unnotched Impact Strengh | | | |
-30℃ (-22℉) |
*** kJ/m² | ISO 180/1U | Dry |
-30℃ (-22℉) |
*** kJ/m² | ISO 180/1U | cond. |
23℃ (73℉) |
*** kJ/m² | ISO 180/1U | Dry |
23℃ (73℉) |
*** kJ/m² | ISO 180/1U | cond. |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness |
*** Mpa
| ISO 2039-1 | Dry |
Ball Indentation Hardness |
*** Mpa
| ISO 2039-1 | cond. |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） |
*** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | 50 N; 120℃/h |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | 50 N; 50℃/h |
Coefficient of Linear Thermal Expansion | | | |
Flow |
*** E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
Across Flow |
*** E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
Melt Temperature(Tm) |
*** °C
| ISO 11357-1/-3 | 10℃/min |
Processing Temperature |
*** °C
| - | Injection molding |
Mould temperature |
*** °C
| - | Injection molding |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | | | |
HB |
*** mm | UL94 | |
HB |
*** mm | UL94 | |
Oxygen Index |
*** %
| ISO 4589 | Method A |
Glow Wire Flammability Index(GWFI) | | | |
2mm |
*** °C | IEC 60695-2-12 | |
FMVSS |
*** -
| FMVSS 302 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity |
*** Ohm-m
| IEC 60093 | Dry |
Volume Resistivity |
*** Ohm-m
| IEC 60093 | cond. |
Surface Resistivity |
*** Ohm
| IEC 60093 | Dry |
Surface Resistivity |
*** Ohm
| IEC 60093 | cond. |
Dielectric Constant(Permittivity) | | | |
100Hz |
*** - | IEC 60250 | Dry |
100Hz |
*** - | IEC 60250 | cond. |
1MHz |
*** - | IEC 60250 | Dry |
1MHz |
*** - | IEC 60250 | cond. |
Dissipation Factor | | | |
100Hz |
*** E-4 | IEC 60250 | Dry |
100Hz |
*** E-4 | IEC 60250 | cond. |
1MHz |
*** E-4 | IEC 60250 | Dry |
1MHz |
*** E-4 | IEC 60250 | cond. |
Comparative Tracking Index (CTI) | | | |
Solution A |
*** V | IEC 60112 | Dry |
Solution B |
*** V | IEC 60112 | Dry |
Dielectric Strength |
*** kV/mm
| IEC 60243-1 | Dry,1 mm |
Dielectric Strength |
*** kV/mm
| IEC 60243-1 | cond. ,1 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.