ULTEM 1000R resin is an amorphous, opaque polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS compliant. ULTEM 1000R resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures with standard flow and standard mold release.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度耐热阻燃耐化学性 | |||
| 添加助剂 | 脱模剂 | |||
| 颜色形状 | 不透明色 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率动态剪切模量-温度应力-应变正割模量-应变比容-温度(pvT) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.27 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
337°C/6.6 kg | 9.7 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | flow, 3.2 mm |
吸水率 | 0.25 % | ASTM D570 | 24 hours |
吸水率 | 1.25 % | ASTM D570 | equilibrium, 23C |
磨耗 | 10 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 110 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 60 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
屈服(yld) | 165 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
弯曲模量 | 3510 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
拉伸模量 | 3580 Mpa | ASTM D638 | 5 mm/min |
泊松比 | 0.36 - | ASTM E 132 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 53 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1335 J/m | ASTM D4812 | |
落锤冲击 | 36 J | ASTM D 3029 | |
反向冲击 | |||
悬臂梁缺口冲击23°C | 1602 J/m | ASTM D 256 | 3.2 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 109 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 210 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 201 °C | ASTM D648 | 6.4 mm, unannealed |
维卡软化温度(Vicat) | 218 °C | ASTM D1525 | Rate B/50 |
相对温度指数(RTI) | |||
冲击Imp,- | 170 °C | UL 746B | |
电气Elec,- | 170 °C | UL 746B | |
强度Str,- | 170 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 55.8 E-6/°C | ASTM E831 | -20°C to 150°C, flow |
横向(Across Flow) | 54 E-6/°C | ASTM E831 | -20°C to 150°C, xflow |
导热系数 | 0.22 W/m-°C | ASTM C 177 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.4 mm | UL94 | |
V-0 | 0.75 mm | UL94 | |
5VA | 3 mm | UL94 | |
氧指数(LOI) | 47 % | ASTM D 2863 | LOI |
NBS 烟密度 | 0.7 - | ASTM E 662 | Flaming, Ds 4 min |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+17 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
1 kHz | 3.15 - | ASTM D 150 | |
耗散因数(DF) | |||
1 kHz | 13 E-4 | ASTM D 150 | |
2450 MHz | 25 E-4 | ASTM D 150 | |
相对漏电起痕指数(CTI ) | |||
- | 4 PLC | UL 746A | |
绝缘强度 | 32.7 kV/mm | ASTM D149 | in air, 1.6 mm |
绝缘强度 | 28 kV/mm | ASTM D149 | in oil, 1.6 mm |
耐电弧性 | 5 PLC | ASTM D495 | Tungsten |
高电压电弧起痕速率(HVTR) | 2 PLC | UL 746A | |
热线圈起燃性(HWI) | 1 PLC | UL 746A | |
高电流电弧起燃性(HAI) | 3 PLC | UL 746A | surface |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。