ULTEMTM 1000F resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217?C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS, US FDA and EU Food Contact compliant, with NSF 51 listing. ULTEMTM 1000F resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHeat ResistanceFlame RetardantFood ContactChemical Resistance | |||
| Appearance | Clear/Transparent | |||
| Compliance | EU 2011/10/ECFDANSFRoHS | |||
| Technical Notes | Food Contact | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateDynamic Shear modulus-temperatureStress-strainSecant modulus-strainSpecific volume-temperature (pvT) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
337°C/6.6 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 3.2 mm |
Water Absorption | *** % | ASTM D570 | 24 hours |
Water Absorption | *** % | ASTM D570 | equilibrium, 23C |
Abrasion resistance | *** mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 5 mm/min |
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Poisson Ratio | *** - | ASTM E 132 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
Falling Dart Impact | *** J | ASTM D 3029 | |
Reverse Impact | |||
Izod, notched 23°C | *** J/m | ASTM D 256 | 3.2 mm |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ASTM D 785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B/50 |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -20°C to 150°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -20°C to 150°C, xflow |
Thermal Conductivity | *** W/m-°C | ASTM C 177 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Oxygen Index | *** % | ASTM D 2863 | LOI |
NBS Smoke Density | *** - | ASTM E 662 | Flaming, Ds 4 min |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
1 kHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
1 kHz | *** E-4 | ASTM D 150 | |
2450 MHz | *** E-4 | ASTM D 150 | |
Comparative Tracking Index (CTI) | |||
- | *** PLC | UL 746A | |
Dielectric Strength | *** kV/mm | ASTM D149 | in air, 1.6 mm |
Dielectric Strength | *** kV/mm | ASTM D149 | in oil, 1.6 mm |
Arc Resistance | *** PLC | ASTM D495 | Tungsten |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746A | |
Hot Wire Ignition(HWI) | *** PLC | UL 746A | |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746A | surface |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.