Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Automative Wheel Covers | |||
| Features | Good SurfaceDimensional StabilityGood PaintablilityChemical Resistance | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 3.2 mm |
Flow | ***~*** % | Internal | flow, annealed 130C 1hr |
Across Flow | ***~*** % | Internal | xflow, 3.2 mm |
Water Absorption | *** % | ASTM D570 | 50% RH, equilib |
Moisture /Humidity Absorption | *** % | ASTM D 570 | 50% RH, 24 hrs |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
Instrumented Impact Energy | |||
-30℃ (-22℉)peak | *** J | ASTM D3763 | |
23℃ (73℉)peak | *** J | ASTM D3763 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B/50 |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 95°C, flow |
Flow | *** E-6/°C | ASTM E831 | 60°C to 138°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 95°C, xflow |
Across Flow | *** E-6/°C | ASTM E831 | 60°C to 138°C, xflow |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
- | *** PLC | UL 746A | |
Arc Resistance | *** PLC | ASTM D495 | Tungsten |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746A | |
Hot Wire Ignition(HWI) | *** PLC | UL 746A | |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | surface |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.