Ultramid A3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. A3EG6 is the preferred grade for producing electrically insulating parts.
Applications
Typical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems.
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性耐热绝缘尺寸稳定填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.36 g/cm³ | ISO 1183 | |
吸水率 | 1.7 % | ISO 62 | 50% RH |
吸水率 | 5.5 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 179 Mpa | ISO 527 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 2.6 % | ISO 527 | Dry,23℃ |
弯曲模量 | 8730 Mpa | ISO 178 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 8.5 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 250 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击Imp,1.5/1.6 mm | 115 °C | UL 746B | |
冲击Imp,3.0/3.2 mm | 120 °C | UL 746B | |
电气Elec,0.71mm | 130 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 125 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 125 °C | UL 746B | |
强度Str,1.5/1.6 mm | 115 °C | UL 746B | |
强度Str,3.0/3.2 mm | 130 °C | UL 746B | |
熔融温度(Tm) | 260 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.71 mm | UL94 | |
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 |