Ultramid A3L HP BK20465 is an unreinforced, heat stabilized, impact modified, high flow, nylon 66 for injection molding. This grade has excellent flow and improved ambient and low temperature toughness.
Applications
Typical applications include fasteners and clamps.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | High ImpactHigh Impact at Low TemperaturHeat StabilizedHigh Flow | |||
| Processing | Injection | |||
| Automotive Specs | FORD WSK-M4D706-AFORD WSS-M4D706-B1GM(General Motors) GMW16447P-PA66-T2Stellantis MS-DB-41 | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | Conditioned,23℃ |
Tensile Modulus | *** Mpa | ISO 527 | Dry,23℃ |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | Conditioned,23℃ |
Yield | *** Mpa | ISO 527 | Dry,23℃ |
Break | *** Mpa | ISO 527 | Conditioned,23℃ |
Break | *** Mpa | ISO 527 | Dry,23℃ |
Tensile Elongation | |||
Yield | *** % | ISO 527 | Conditioned,23℃ |
Yield | *** % | ISO 527 | Dry,23℃ |
Nominal Tensile Strain at Break | *** % | ISO 527 | Conditioned,23℃ |
Nominal Tensile Strain at Break | *** % | ISO 527 | Dry,23℃ |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned,23℃ |
Flexural Modulus | *** Mpa | ISO 178 | Dry,23℃ |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Conditioned,23℃ |
- | *** Mpa | ISO 178 | Dry,23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180 | Conditioned |
-40℃ (-40℉) | *** kJ/m² | ISO 180 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 180 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | Dry |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Melt Temperature(Tm) | *** °C | ISO 3146 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.