Ultramid A3EG6 is a 30% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
Applications
Typical applications include such as lamp socket housings, cooling fans, insulating profiles for aluminium window frames, and electrical insulation parts.
| Original Document | Technical Datasheet-ISO(English) Technical Datasheet-ASTM(English) | |||
| Resin ID | PA66-GF30 | |||
| Features | High Stiffness/RigidityInsulatingDimensional StabilityFilled & Reinforced | |||
| Processing | Injection | |||
| Automotive Specs | FORD WSK-M4D642-AStellantis MS-DB-41 | |||
| Technical Notes | Shear modulus-TemperatureMoisture absorption-Relative humidityWater absorption-TimeDielectric strength-Moisture contentSpecific volume resistivity-Temperature | |||
| Diagrams | Viscosity-shear rate 280|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|28.7:541.101@59.1:432.9@121.5:340.9@249.9:263@514.1:197.399@1057.6:143.3@2175.7:99.8001@4475.7:66.1001@9207:41.3@18940:24.1{n}290|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|43.8:354.701@90.09999999999999:283.8@185.3:223.5@381.2:172.4@784.3:129.399@1613.3:93.90009999999999@3318.9:65.40000000000001@6827.3:43.3@14044.6:27.1@28891.5:15.8{n}300|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|64.90000000000001:239.401@133.5:191.5@274.6:150.8@565:116.3@1162.2:87.29989999999999@2390.8:63.4001@4918.1:44.2@10117.2:29.3@20812.4:18.3@42813.6:10.6Shearstress-shear rate 280|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|28.7:15529.6@59.1:25584.4@121.5:41419.4@249.9:65723.7@514.1:101483@1057.6:151554@2175.7:217135@4475.7:295844@9207:380249@18940:456454{n}290|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|43.8:15535.9@90.09999999999999:25570.4@185.3:41414.6@381.2:65718.89999999999@784.3:101488@1613.3:151489@3318.9:217056@6827.3:295622@14044.6:380609@28891.5:456486{n}300|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|64.90000000000001:15537.1@133.5:25565.2@274.6:41409.7@565:65709.5@1162.2:101460@2390.8:151577@4918.1:217380@10117.2:296434@20812.4:380867@42813.6:453824Stress-strain -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.32:34.6@0.64:66.89@0.96:96.48999999999999@1.28:123.35@1.6:147.66@1.92:169.7@2.24:189.73@2.56:207.9@2.88:224.08@3.2:237.78{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.29:31.43@0.58:60.49@0.87:86.90000000000001@1.16:110.68@1.45:131.96@1.74:150.97@2.03:167.88@2.32:182.7@2.61:195.23@2.9:204.92{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.31:32.89@0.62:62.78@0.93:89.31@1.24:112.45@1.55:132.37@1.86:149.28@2.17:163.29@2.48:174.32@2.79:181.89@3.1:185.05{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.32:31.71@0.64:59.62@0.96:83.62@1.28:103.87@1.6:120.67@1.92:134.37@2.24:145.26@2.56:153.44@2.88:158.76@3.2:160.65{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.42:31.97@0.84:56.46@1.26:75.86@1.68:91.62@2.1:104.46@2.52:114.63@2.94:122.12@3.36:126.87@3.78:128.99@4.2:129.01{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.51:29.13@1.02:50.84@1.53:67.86@2.04:81.64@2.55:92.73@3.06:101.14@3.57:106.75@4.08:109.66@4.59:110.6@5.1:111.26{n}100|%|Mpa|Strain in %|Stress in MPa|0:0@0.52:25.89@1.04:45.58@1.56:61.05@2.08:73.40000000000001@2.6:83.17@3.12:90.5@3.64:95.47@4.16:98.28@4.68:99.54000000000001@5.2:100.48{n}120|%|Mpa|Strain in %|Stress in MPa|0:0@0.52:23.91@1.04:42.08@1.56:56.17@2.08:67.23@2.6:75.84999999999999@3.12:82.34@3.64:86.88@4.16:89.68000000000001@4.68:91.16@5.2:92.09{n}140|%|Mpa|Strain in %|Stress in MPa|0:0@0.55:23.45@1.1:40.79@1.65:53.79@2.2:63.63@2.75:71.08@3.3:76.56@3.85:80.34@4.4:82.64@4.95:83.75@5.5:84.19{n}160|%|Mpa|Strain in %|Stress in MPa|0:0@0.5600000000000001:22.24@1.12:38.17@1.68:49.78@2.24:58.42@2.8:64.93000000000001@3.36:69.79000000000001@3.92:73.26000000000001@4.48:75.5@5.04:76.73@5.6:77.33Stress-strain (Cond.) -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.3:35.38@0.6:67.67@0.9:96.65000000000001@1.2:122.42@1.5:145.34@1.8:165.81@2.1:184.21@2.4:200.68@2.7:215.03@3:226.6{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.33:37.78@0.66:71.28@0.99:100.28@1.32:125.04@1.65:146.11@1.98:164.11@2.31:179.45@2.64:192.17@2.97:201.64@3.3:206.36{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.37:37.29@0.74:68.44@1.11:94.38@1.48:115.81@1.85:133.22@2.22:146.97@2.59:157.29@2.96:164.38@3.33:168.43@3.7:169.64{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.37:28.16@0.74:50.46@1.11:68.59@1.48:83.68000000000001@1.85:96.34999999999999@2.22:106.89@2.59:115.34@2.96:121.64@3.33:125.69@3.69:127.388@4.1:127.395{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.45:27.16@0.9:48.11@1.35:64.84999999999999@1.8:78.48@2.25:89.47@2.7:97.90000000000001@3.15:103.74@3.6:107.08@4.05:108.43@4.5:108.93{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.46:25.1@0.92:44.5@1.38:59.81@1.84:71.98999999999999@2.3:81.53@2.76:88.63@3.22:93.41@3.68:96.09999999999999@4.14:97.2@4.6:97.73{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.47:22.69@0.9399999999999999:40.16@1.41:53.77@1.88:64.40000000000001@2.35:72.56999999999999@2.82:78.59@3.29:82.67@3.76:85.08@4.23:86.25@4.7:86.95999999999999{n}100|%|Mpa|Strain in %|Stress in MPa|0:0@0.49:21.4@0.98:37.66@1.47:50.18@1.96:59.87@2.45:67.26000000000001@2.94:72.64@3.43:76.23@3.92:78.28@4.41:79.25@4.9:79.94{n}120|%|Mpa|Strain in %|Stress in MPa|0:0@0.51:20.25@1.02:35.44@1.53:46.92@2.04:55.61@2.55:62.11@3.06:66.81999999999999@3.57:70@4.08:71.86@4.59:72.68000000000001@5.1:72.87{n}160|%|Mpa|Strain in %|Stress in MPa|0:0@0.48:16.74@0.96:28.86@1.44:37.81@1.92:44.6@2.4:49.85@2.88:53.92@3.36:57@3.84:59.2@4.32:60.65@4.8:61.61Secant modulus-strain -40|%|MPa|Strain in %|Secant modulus in MPa|0.32:10812.5@0.64:10451.6@0.96:10051@1.28:9636.719999999999@1.6:9228.75@1.92:8838.540000000001@2.24:8470.09@2.56:8121.09@2.88:7780.56@3.2:7430.62{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.29:10837.9@0.58:10429.3@0.87:9988.51@1.16:9541.379999999999@1.45:9100.690000000001@1.74:8676.440000000001@2.03:8269.950000000001@2.32:7875@2.61:7480.08@2.9:7066.21{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.31:10609.7@0.62:10125.8@0.93:9603.23@1.24:9068.549999999999@1.55:8540@1.86:8025.81@2.17:7524.88@2.48:7029.03@2.79:6519.35@3.1:5969.35{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.32:9909.379999999999@0.64:9315.620000000001@0.96:8710.42@1.28:8114.84@1.6:7541.88@1.92:6998.44@2.24:6484.82@2.56:5993.75@2.88:5512.5@3.2:5020.31{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.42:7611.9@0.84:6721.43@1.26:6020.63@1.68:5453.57@2.1:4974.29@2.52:4548.81@2.94:4153.74@3.36:3775.89@3.78:3412.43@4.2:3071.67{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.51:5711.76@1.02:4984.31@1.53:4435.29@2.04:4001.96@2.55:3636.47@3.06:3305.23@3.57:2990.2@4.08:2687.75@4.59:2409.59@5.1:2181.57{n}100|%|MPa|Strain in %|Secant modulus in MPa|0.52:4978.85@1.04:4382.69@1.56:3913.46@2.08:3528.85@2.6:3198.85@3.12:2900.64@3.64:2622.8@4.16:2362.5@4.68:2126.92@5.2:1932.31{n}120|%|MPa|Strain in %|Secant modulus in MPa|0.52:4598.08@1.04:4046.15@1.56:3600.64@2.08:3232.21@2.6:2917.31@3.12:2639.1@3.64:2386.81@4.16:2155.77@4.68:1947.86@5.2:1770.96{n}140|%|MPa|Strain in %|Secant modulus in MPa|0.55:4263.64@1.1:3708.18@1.65:3260@2.2:2892.27@2.75:2584.73@3.3:2320@3.85:2086.75@4.4:1878.18@4.95:1691.92@5.5:1530.73{n}160|%|MPa|Strain in %|Secant modulus in MPa|0.5600000000000001:3971.43@1.12:3408.04@1.68:2963.1@2.24:2608.04@2.8:2318.93@3.36:2077.08@3.92:1868.88@4.48:1685.27@5.04:1522.42@5.6:1380.89Secant modulus-strain (Cond.) -40|%|MPa|Strain in %|Secant modulus in MPa|0.3:11793.3@0.6:11278.3@0.9:10738.9@1.2:10201.7@1.5:9689.33@1.8:9211.67@2.1:8771.9@2.4:8361.67@2.7:7964.07@3:7553.33{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.33:11448.5@0.66:10800@0.99:10129.3@1.32:9472.73@1.65:8855.15@1.98:8288.379999999999@2.31:7768.4@2.64:7279.17@2.97:6789.23@3.3:6253.33{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.37:10078.4@0.74:9248.65@1.11:8502.700000000001@1.48:7825@1.85:7201.08@2.22:6620.27@2.59:6072.97@2.96:5553.38@3.33:5057.96@3.7:4584.86{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.37:7610.81@0.74:6818.92@1.11:6179.28@1.48:5654.05@1.85:5208.11@2.22:4814.86@2.59:4453.28@2.96:4109.46@3.33:3774.47@3.69:3452.25@4.1:3107.2{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.45:6035.56@0.9:5345.56@1.35:4803.7@1.8:4360@2.25:3976.44@2.7:3625.93@3.15:3293.33@3.6:2974.44@4.05:2677.28@4.5:2420.67{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.46:5456.52@0.92:4836.96@1.38:4334.06@1.84:3912.5@2.3:3544.78@2.76:3211.23@3.22:2900.93@3.68:2611.41@4.14:2347.83@4.6:2124.57{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.47:4827.66@0.9399999999999999:4272.34@1.41:3813.48@1.88:3425.53@2.35:3088.09@2.82:2786.88@3.29:2512.77@3.76:2262.77@4.23:2039.01@4.7:1850.21{n}100|%|MPa|Strain in %|Secant modulus in MPa|0.49:4367.35@0.98:3842.86@1.47:3413.61@1.96:3054.59@2.45:2745.31@2.94:2470.75@3.43:2222.45@3.92:1996.94@4.41:1797.05@4.9:1631.43{n}120|%|MPa|Strain in %|Secant modulus in MPa|0.51:3970.59@1.02:3474.51@1.53:3066.67@2.04:2725.98@2.55:2435.69@3.06:2183.66@3.57:1960.78@4.08:1761.27@4.59:1583.44@5.1:1428.82{n}160|%|MPa|Strain in %|Secant modulus in MPa|0.48:3487.5@0.96:3006.25@1.44:2625.69@1.92:2322.92@2.4:2077.08@2.88:1872.22@3.36:1696.43@3.84:1541.67@4.32:1403.94@4.8:1283.54Stress-strain (isochronous)(Creep) 23°C (cond.) 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1442:9.800000000000001@0.2526:16.5@0.3731:23.2@0.5082:29.9@0.66:36.6@0.8300999999999999:43.3@1.02:50@1.2306:56.7@1.4628:63.4@1.7132:70{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.1463:9.800000000000001@0.2606:16.5@0.3915:23.2@0.5416:29.9@0.7124:36.6@0.9048:43.3@1.1192:50@1.3553:56.7@1.6126:63.4@1.8861:70{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.1496:9.800000000000001@0.2725:16.5@0.4181:23.2@0.5888:29.9@0.7849:36.6@1.0059:43.3@1.2506:50@1.5169:56.7@1.8026:63.4@2.1008:70{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.1544:9.800000000000001@0.2899:16.5@0.4566:23.2@0.6554:29.9@0.8851:36.6@1.1427:43.3@1.4246:50@1.7264:56.7@2.0438:63.4@2.3675:70{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.1617:9.800000000000001@0.3156:16.5@0.512:23.2@0.7496:29.9@1.0237:36.6@1.3279:43.3@1.655:50@1.9979:56.7@2.3498:63.4@2.6989:70Stress-strain (isochronous)(Creep) 60°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1139:5.9@0.2671:11.9@0.4433:17.9@0.6371:23.9@0.8453000000000001:29.9@1.0658:35.9@1.2969:41.9@1.5374:47.9@1.7861:53.9@2.0465:60{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.121:5.9@0.2859:11.9@0.4752:17.9@0.6823:23.9@0.9033:29.9@1.1354:35.9@1.3764:41.9@1.6248:47.9@1.8792:53.9@2.1427:60{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.1292:5.9@0.3073:11.9@0.5113:17.9@0.7332:23.9@0.9679:29.9@1.2123:35.9@1.4636:41.9@1.7199:47.9@1.9796:53.9@2.2457:60{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.1387:5.9@0.3318:11.9@0.5522:17.9@0.7902:23.9@1.0399:29.9@1.2973:35.9@1.5592:41.9@1.8233:47.9@2.088:53.9@2.356:60{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.1495:5.9@0.3597:11.9@0.5985:17.9@0.8542999999999999:23.9@1.1202:29.9@1.3912:35.9@1.6639:41.9@1.9358:47.9@2.2049:53.9@2.4739:60Stress-strain (isochronous)(Creep) 90°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.2017:5.9@0.4057:11.9@0.6139:17.9@0.833:23.9@1.0709:29.9@1.3358:35.9@1.6356:41.9@1.977:47.9@2.3649:53.9@2.8095:60{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.2135:5.9@0.4296:11.9@0.6503:17.9@0.8833:23.9@1.1375:29.9@1.4219:35.9@1.7454:41.9@2.1156:47.9@2.5379:53.9@3.0236:60{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.2267:5.9@0.4561:11.9@0.6909:17.9@0.9395:23.9@1.2118:29.9@1.518:35.9@1.868:41.9@2.2702:47.9@2.731:53.9@3.2628:60{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2413:5.9@0.4857:11.9@0.7361:17.9@1.0021:23.9@1.2946:29.9@1.6251:35.9@2.0047:41.9@2.4428:47.9@2.9467:53.9@3.5301:60{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.2576:5.9@0.5185999999999999:11.9@0.7865:17.9@1.0718:23.9@1.3869:29.9@1.7446:35.9@2.1572:41.9@2.6356:47.9@3.1876:53.9@3.8287:60Stress-strain (isochronous)(Creep) 120°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1874:5.9@0.375:11.4@0.5797:16.9@0.8056:22.4@1.057:27.9@1.3381:33.4@1.6531:38.9@2.0062:44.4@2.4014:49.9@2.809:55{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.1981:5.9@0.3974:11.4@0.6155:16.9@0.8574000000000001:22.4@1.1278:27.9@1.431:33.4@1.7718:38.9@2.1544:44.4@2.5832:49.9@3.0257:55{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.2105:5.9@0.4229:11.4@0.6565:16.9@0.9166:22.4@1.2083:27.9@1.5365:33.4@1.9062:38.9@2.3219:44.4@2.7882:49.9@3.2696:55{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2247:5.9@0.4522:11.4@0.7034:16.9@0.9841:22.4@1.2999:27.9@1.6563:33.4@2.0584:38.9@2.5111:44.4@3.0192:49.9@3.5439:55{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.241:5.9@0.4858:11.4@0.757:16.9@1.0611:22.4@1.4042:27.9@1.7923:33.4@2.2308:38.9@2.7249:44.4@3.2797:49.9@3.8524:55Stress-strain (isochronous)(Creep) 140°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.2214:5.9@0.412:10.8@0.6131:15.7@0.8288:20.6@1.0635:25.5@1.3212:30.4@1.6062:35.3@1.9227:40.2@2.2751:45.1@2.6675:50{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.2338:5.9@0.4359:10.8@0.6501:15.7@0.8814:20.6@1.1344:25.5@1.4142:30.4@1.7255:35.3@2.0734:40.2@2.463:45.1@2.8994:50{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.2478:5.9@0.4629:10.8@0.6921:15.7@0.9409999999999999:20.6@1.2151:25.5@1.52:30.4@1.8615:35.3@2.2454:40.2@2.6778:45.1@3.1647:50{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2637:5.9@0.4935:10.8@0.7397:15.7@1.0086:20.6@1.3066:25.5@1.6403:30.4@2.0164:35.3@2.4417:40.2@2.9234:45.1@3.4684:50{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.2816:5.9@0.5281:10.8@0.7936:15.7@1.0854:20.6@1.4107:25.5@1.7773:30.4@2.193:35.3@2.6658:40.2@3.204:45.1@3.8161:50Creep modulus-time 23°C (cond.) 10|h|MPa|Time in h|Creep modulus in MPa|10:6789.54@100:6689.13@1000:6537.6@10000:6328.98@100000:6036.33{n}20|h|MPa|Time in h|Creep modulus in MPa|10:6371.96@100:6121.22@1000:5787.83@10000:5361.81@100000:4843.3{n}30|h|MPa|Time in h|Creep modulus in MPa|10:5878.45@100:5514.76@1000:5071.5@10000:4555.07@100000:3981.75{n}40|h|MPa|Time in h|Creep modulus in MPa|10:5376.81@100:4954.78@1000:4474.29@10000:3950.43@100000:3404.97{n}50|h|MPa|Time in h|Creep modulus in MPa|10:4901.96@100:4467.48@1000:3998.08@10000:3509.76@100000:3021.15{n}60|h|MPa|Time in h|Creep modulus in MPa|10:4471.09@100:4056.29@1000:3625.04@10000:3189.85@100000:2764.27{n}70|h|MPa|Time in h|Creep modulus in MPa|10:4085.92@100:3711.36@1000:3332.06@10000:2956.71@100000:2593.65Creep modulus-time 60°C 10|h|MPa|Time in h|Creep modulus in MPa|10:4649.28@100:4350.78@1000:4053.53@10000:3758.58@100000:3470.81{n}20|h|MPa|Time in h|Creep modulus in MPa|10:3927.35@100:3664.28@1000:3406.36@10000:3155.87@100000:2913.85{n}30|h|MPa|Time in h|Creep modulus in MPa|10:3534.07@100:3307.3@1000:3086.73@10000:2873.19@100000:2667.41{n}40|h|MPa|Time in h|Creep modulus in MPa|10:3271.6@100:3078.78@1000:2891.42@10000:2710.14@100000:2535.61{n}50|h|MPa|Time in h|Creep modulus in MPa|10:3079.77@100:2918.53@1000:2761.71@10000:2609.62@100000:2462.51{n}60|h|MPa|Time in h|Creep modulus in MPa|10:2931.83@100:2800.21@1000:2671.77@10000:2546.69@100000:2425.32Creep modulus-time 90°C 10|h|MPa|Time in h|Creep modulus in MPa|10:2932.83@100:2769.94@1000:2609.13@10000:2450.44@100000:2295.25{n}20|h|MPa|Time in h|Creep modulus in MPa|10:2902.92@100:2739.68@1000:2577.79@10000:2418.7@100000:2263.03{n}30|h|MPa|Time in h|Creep modulus in MPa|10:2790.51@100:2627.04@1000:2465.89@10000:2308.11@100000:2154.43{n}40|h|MPa|Time in h|Creep modulus in MPa|10:2603.48@100:2441.73@1000:2283.33@10000:2129.34@100000:1980.37{n}50|h|MPa|Time in h|Creep modulus in MPa|10:2373.22@100:2215.56@1000:2062.7@10000:1915.14@100000:1773.43{n}60|h|MPa|Time in h|Creep modulus in MPa|10:2135.61@100:1984.39@1000:1838.91@10000:1699.67@100000:1567.11Creep modulus-time 120°C 10|h|MPa|Time in h|Creep modulus in MPa|10:3069.88@100:2898.48@1000:2725.02@10000:2549.67@100000:2374.36{n}20|h|MPa|Time in h|Creep modulus in MPa|10:2840.35@100:2671.67@1000:2501.55@10000:2332.04@100000:2164.61{n}30|h|MPa|Time in h|Creep modulus in MPa|10:2584.86@100:2420.44@1000:2257.27@10000:2096.56@100000:1939.51{n}40|h|MPa|Time in h|Creep modulus in MPa|10:2324.76@100:2168.13@1000:2014.51@10000:1864.96@100000:1720.36{n}50|h|MPa|Time in h|Creep modulus in MPa|10:2075.49@100:1929.37@1000:1787.47@10000:1650.67@100000:1519.54{n}55|h|MPa|Time in h|Creep modulus in MPa|10:1957.99@100:1817.76@1000:1682.16@10000:1551.96@100000:1427.68Creep modulus-time 140°C 10|h|MPa|Time in h|Creep modulus in MPa|10:2629.74@100:2486.35@1000:2342.19@10000:2197.73@100000:2054.52{n}20|h|MPa|Time in h|Creep modulus in MPa|10:2495.47@100:2347.4@1000:2199.55@10000:2052.88@100000:1908.36{n}30|h|MPa|Time in h|Creep modulus in MPa|10:2309.11@100:2157.89@1000:2008.27@10000:1861.54@100000:1718.56{n}40|h|MPa|Time in h|Creep modulus in MPa|10:2095.18@100:1943.2@1000:1794.63@10000:1650.61@100000:1512.09{n}50|h|MPa|Time in h|Creep modulus in MPa|10:1874.41@100:1724.49@1000:1579.93@10000:1441.59@100000:1310.24Specific volume-temperature (pvT) 0.1|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.72294@30:0.72519@40:0.72746@50:0.72972@60:0.732@70:0.73429@80:0.73659@90:0.73892@100:0.74127@110:0.74365@120:0.74607@130:0.74855@140:0.7511@150:0.75374@160:0.75651@170:0.75943@180:0.76256@190:0.76596@200:0.76972@210:0.77393@220:0.77873@230:0.78431@240:0.7909@250:0.7988@260:0.80841@270:0.82024@275:0.827@280:0.8297@290:0.83509@300:0.84048{n}40|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.71873@30:0.72084@40:0.72296@50:0.72507@60:0.72719@70:0.72931@80:0.73144@90:0.73358@100:0.7357399999999999@110:0.73792@120:0.74014@130:0.74239@140:0.7447@150:0.74708@160:0.74957@170:0.75219@180:0.75497@190:0.7579900000000001@200:0.7613@210:0.765@220:0.76922@230:0.7740899999999999@240:0.77983@250:0.78671@260:0.79506@270:0.80533@277.58:0.8131@280:0.81426@290:0.8190499999999999@300:0.82382{n}80|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.71478@30:0.71677@40:0.71875@50:0.72073@60:0.72271@70:0.7246899999999999@80:0.72667@90:0.72865@100:0.73064@110:0.73265@120:0.73468@130:0.73675@140:0.73885@150:0.74102@160:0.74327@170:0.7456199999999999@180:0.74812@190:0.75081@200:0.75376@210:0.75703@220:0.76074@230:0.76502@240:0.77005@250:0.77605@260:0.78333@270:0.79227@280:0.80339@280.16:0.8015600000000001@290:0.80586@300:0.8102{n}120|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.71106@30:0.71293@40:0.7148@50:0.71666@60:0.71851@70:0.72036@80:0.72221@90:0.72406@100:0.7259100000000001@110:0.72777@120:0.72965@130:0.73154@140:0.73347@150:0.73545@160:0.7375@170:0.73963@180:0.74188@190:0.7443@200:0.74692@210:0.74984@220:0.75312@230:0.75689@240:0.76131@250:0.76657@260:0.77293@270:0.78073@280:0.7904099999999999@282.74:0.79172@290:0.79465@300:0.79867{n}160|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.7075399999999999@30:0.70931@40:0.71108@50:0.71283@60:0.71457@70:0.71631@80:0.71804@90:0.71977@100:0.72149@110:0.72322@120:0.72496@130:0.72671@140:0.72849@150:0.73031@160:0.7321800000000001@170:0.73412@180:0.73616@190:0.73833@200:0.74069@210:0.74329@220:0.74621@230:0.74955@240:0.75344@250:0.75806@260:0.76363@270:0.77045@280:0.77889@285.32:0.7831399999999999@290:0.78491@300:0.78868{n}200|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.7042@30:0.70589@40:0.70755@50:0.70921@60:0.71086@70:0.71249@80:0.71412@90:0.71574@100:0.71735@110:0.71897@120:0.72058@130:0.72221@140:0.7238599999999999@150:0.72553@160:0.72724@170:0.72902@180:0.73088@190:0.73285@200:0.73497@210:0.7373@220:0.7399@230:0.74287@240:0.74631@250:0.75037@260:0.75526@270:0.76122@280:0.76859@287.9:0.77554@290:0.7763@300:0.77986Coefficient of Linear Thermal Expansion(CTE)-Temperature αn|°C|%|Temperature in °C|ΔL/L0 in %|-50:-0.521@-40:-0.474@-30:-0.41@-20:-0.338@-10:-0.262@0:-0.184@10:-0.102@20:-0.025@24:0.008@30:0.057@40:0.14@50:0.232@54:0.272@60:0.335@70:0.453@80:0.583@90:0.72@100:0.869@110:1.023@120:1.19@130:1.362@140:1.544@150:1.728@160:1.919@170:2.105@180:2.288@190:2.465{n}αp|°C|%|Temperature in °C|ΔL/L0 in %|-50:-0.193@-40:-0.171@-30:-0.146@-20:-0.12@-10:-0.092@0:-0.065@10:-0.037@20:-0.008999999999999999@24:0.003@30:0.019@40:0.047@50:0.074@54:0.08500000000000001@60:0.101@70:0.125@80:0.147@90:0.168@100:0.189@110:0.21@120:0.231@130:0.252@140:0.273@150:0.295@160:0.316@170:0.336@180:0.356@190:0.376Tensile modulus-temperature |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:10487@-30:10438@-20:10372@-10:10454@0:10451@10:10376@20:10309@30:10044@40:9307@50:7819@60:6704@70:5880@80:5321@90:4999@100:4759@110:4577@120:4411@130:4261@140:4116@150:3994@160:3825Tensile modulus-temperature (cond.) |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:11007@-30:10818@-20:10714@-10:10239@0:9823@10:7889@20:6903@30:6338@40:5711@50:5427@60:5209@70:4905@80:4610@90:4406@100:4180@110:4000@120:3801@130:3672@140:3549@150:3426@160:3263 | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
275°C/5 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
- | *** % | Internal | |
Water Absorption | *** % | ASTM D570 | 50% RH |
Water Absorption | *** % | ASTM D570 | Saturation |
Water Absorption | *** % | ISO 62 | 50% RH |
Water Absorption | *** % | ISO 62 | Saturation |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | Conditioned,23℃ |
Tensile Modulus | *** Mpa | ISO 527 | Dry,23℃ |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | Conditioned |
Break | *** Mpa | ISO 527 | Conditioned,23℃ |
Break | *** Mpa | ISO 527 | Dry,-40℃ |
Break | *** Mpa | ISO 527 | Dry,23℃ |
Break | *** Mpa | ASTM D638 | Dry,23℃ |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Dry,23℃ |
Break | *** % | ISO 527 | Conditioned |
Break | *** % | ISO 527 | Conditioned,23℃ |
Break | *** % | ISO 527 | Dry,-40℃ |
Break | *** % | ISO 527 | Dry,23℃ |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned,23℃ |
Flexural Modulus | *** Mpa | ISO 178 | Dry,23℃ |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Conditioned,23℃ |
- | *** Mpa | ISO 178 | Dry,23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** J/m | ASTM D256 | Dry |
23℃ (73℉) | *** J/m | ASTM D256 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | Dry |
Relative Temperature Index(RTI), Imp | |||
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | Internal | Dry |
Across Flow | *** E-6/°C | Internal | Dry |
- | *** E-6 mm/mm/℃ | ASTM D E831 | Dry |
Melt Temperature(Tm) | *** °C | ASTM D3418 | Dry |
Melt Temperature(Tm) | *** °C | ISO 3146 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | ASTM D257 | Conditioned,1.50 mm |
Volume Resistivity | *** Ohm-m | ASTM D257 | Dry,1.50 mm |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Volume Resistivity | *** Ohm-m | IEC 60093 | Conditioned |
Dielectric Constant(Permittivity) | |||
1MHz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | Conditioned |
Dissipation Factor | |||
100Hz | *** E-4 | IEC 60250 | |
100Hz | *** E-4 | IEC 60250 | Conditioned |
1MHz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | Conditioned |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | Conditioned |
- | *** V | IEC 60112 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.
| Chinese | English | File Format | Action |
|---|---|---|---|
| 物性表-ISO(英文) | Technical Datasheet-ISO(English) | Down Load | |
| 物性表-ASTM(英文) | Technical Datasheet-ASTM(English) | Down Load |
| Supplier | Price | Region | Message | Contact |
|---|
| Group | Value |
|---|