Ultramid 8253 HS BK102 is a heat stabilized, pigmented black, impact modified type 6 nylon graft copolymer developed for both injection molding and extrusion applications. It exhibits varying levels of toughness and flexibility combined with excellent thermal and chemical properties.
Applications
Ultramid 8253 HS BK102 is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips fasteners, flanges, key housings as well as many flexible tubing applications.
| Original Document | Technical Datasheet-ISO(English) Technical Datasheet-ASTM(English) | |||
| Features | High ImpactGood ToughnessHeat Stabilized | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | InjectionExtrusion | |||
| Automotive Specs | FORD WSK-M4D578-AGM(General Motors) GMW17576-PA6-T1Stellantis MS-DB-41 | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
- | *** % | Internal | 3.18 mm |
Water Absorption | *** % | ASTM D570 | 24 hr |
Water Absorption | *** % | ASTM D570 | 50% RH |
Water Absorption | *** % | ASTM D570 | Saturation |
Water Absorption | *** % | ISO 62 | 24 hr |
Water Absorption | *** % | ISO 62 | 50% RH |
Water Absorption | *** % | ISO 62 | Saturation |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | Dry,23℃ |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Dry,23℃ |
Yield | *** Mpa | ISO 527 | Dry,23℃ |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Dry,23℃ |
Yield | *** % | ISO 527 | Dry,23℃ |
Break | *** % | ASTM D638 | Dry,23℃ |
Nominal Tensile Strain at Break | *** % | ISO 527 | Dry,23℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Dry,23℃ |
Flexural Modulus | *** Mpa | ISO 178 | Dry,23℃ |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | Dry,23℃ |
- | *** Mpa | ISO 178 | Dry,23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180 | Dry |
Falling Dart Impact | *** J | Internal | Dry,23℃ |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | Dry |
Relative Temperature Index(RTI), Imp | |||
0.71mm | *** °C | UL 746B | |
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.71mm | *** °C | UL 746B | |
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
0.71mm | *** °C | UL 746B | |
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
6.0mm | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6 mm/mm/℃ | ASTM D E831 | Dry |
Melt Temperature(Tm) | *** °C | ASTM D3418 | Dry |
Melt Temperature(Tm) | *** °C | ISO 3146 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.