Ultramid 8232G HS FR BK102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature.
Applications
Ultramid 8232G HS FR BK102 is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings.
| Original Document | Technical Datasheet-ISO(English) Technical Datasheet-ASTM(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat ResistanceFlame RetardantFilled & Reinforced | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 25% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
- | *** % | Internal | 3.18 mm |
Water Absorption | *** % | ASTM D570 | 50% RH |
Water Absorption | *** % | ASTM D570 | Saturation |
Water Absorption | *** % | ISO 62 | 50% RH |
Water Absorption | *** % | ISO 62 | Saturation |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | Dry,23℃ |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | Dry,23℃ |
Break | *** Mpa | ASTM D638 | Dry,23℃ |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Dry,23℃ |
Break | *** % | ISO 527 | Dry,23℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Dry,23℃ |
Flexural Modulus | *** Mpa | ISO 178 | Dry,23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180 | Dry |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | Dry |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
2.5mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
2.5mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
2.5mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Melt Temperature(Tm) | *** °C | ASTM D3418 | Dry |
Melt Temperature(Tm) | *** °C | ISO 3146 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
5VA | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.