NORYL GTX975 resin is a conductive, 18% mineral reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade combines high stiffness and excellent temperature resistance with conductivity for primerless electrostatic painting. NORYL GTX975 was designed for in- or on-line painted exterior automotive trim parts such as tank flaps and corner panels.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性高冲击耐热导电良好表面尺寸稳定低翘曲低收缩耐化学性耐水解低密度低吸湿性填充增强 | |||
| 成型方式 | 注塑静电/粉末喷涂 | |||
| 增强填充 | 18% 矿物 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
比重 | 1.25 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
280°C/5.0 kg | 10 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
280°C/5.0 kg | 15 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.8~1.2 % | Internal | flow, 3.2 mm |
吸水率 | 3.5 % | ISO 62 | 23°C/sat |
吸湿率 | 1.1 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 69 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 65 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 65 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 68 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 3.5 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 3.5 % | ISO 527 | 5 mm/min |
断裂(brk) | 4.5 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 4 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 113 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 110 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 4000 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 4000 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 4450 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 4200 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 3 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 35 kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 40 kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 30 J/m | ASTM D256 | |
-30℃ (-22℉) | 4 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 35 J/m | ASTM D256 | |
23℃ (73℉) | 4 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | 35 kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | 40 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 3 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 210 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 185 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 215 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 200 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 195 °C | ISO 306 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 54 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 50 E-6/°C | ISO 11359-2 | 23°C to 60°C, flow |
横向(Across Flow) | 60 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 65 E-6/°C | ISO 11359-2 | 23°C to 60°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1E+3~1E+4 cm³/10 min | Internal |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。