MVR (300°C/1.2 kg) 12 cm³/10 min; medium viscosity; easy release; injection molding - melt temperature 280 - 320°C; available in black colors only; automotive exterior roof trim + pillar appliques; optimized and especially suitable for high-gloss surfaces with highest requirements "Piano-black"; tailored for the use in combination with Polysiloxan coatings
| Original Document | Technical Datasheet-ISO(English) Technical Datasheet-ISO(Chinese) | |||
| Features | Good SurfaceHigh GlossMirror surfaceGood PaintablilityMold ReleaseMedium viscosity | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
300°C/1.2 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 60x60x2 mm; 500 bar |
Flow | ***~*** % | ISO 2577 | |
Across Flow | *** % | ISO 294-4 | 60x60x2 mm; 500 bar |
Across Flow | ***~*** % | ISO 2577 | |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
Water Absorption | *** % | ISO 62 | Saturation, 23°C |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Break | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Break | *** % | ISO 527-1/-2 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2 mm/min |
3.5% strain | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strain | |||
- | *** % | ISO 178 | 2 mm/min |
Puncture | |||
Force | *** N | ISO 6603-2 | -30℃ |
Force | *** N | ISO 6603-2 | 23℃ |
Energy | *** J | ISO 6603-2 | -30℃ |
Energy | *** J | ISO 6603-2 | 23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | 3 mm,complete break |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | 3 mm,partial break |
Charpy Unnotched Impact Strengh | |||
-60℃ (-76℉) | *** kJ/m² | ISO 179/1eU | |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | 3 mm,complete break |
23℃ (73℉) | *** kJ/m² | ISO 180/A | 3 mm,partial break |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 120 °C/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 50°C/h |
Relative Temperature Index(RTI), Imp | |||
1.5/1.6 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
1.5/1.6 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
1.5/1.6 mm | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Glass Transition Temperature | *** °C | ISO 11357-1/-2 | 10°C/min |
Thermal Conductivity | *** W/(m K) | ISO 8302 | cross-flow |
Ball Pressure Test | *** °C | IEC 60695-10-2 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
FMVSS | *** pass | FMVSS 302 | >=1.0 mm |
Flash ignition temperature | *** °C | ASTM D 1929 | |
Self ignition temperature | *** °C | ASTM D 1929 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
100Hz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Solution B | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | 1 mm |
Electrolytical Corrosion | *** - | IEC 60426 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Water Vapor Transmission Rate | *** g/m²/24 hr | ISO 15106-1 | 23 °C; 85 % RH; 100 µm film |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.