MVR (300°C/1.2 kg) 6.0 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; easy release; injection molding - melt temperature 310 - 330°C; available in opaque colors only
| Original Document | Technical Datasheet-ISO(English) Technical Datasheet-ISO(Chinese) | |||
| Features | Flame RetardantMold ReleaseHigh ViscosityFilled & Reinforced | |||
| Appearance | Pellets/GranulesOpaque Color | |||
| Processing | Injection | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateDynamic Shear modulus-temperatureStress-strain(Yield)Secant modulus-strain(Yield)Specific volume-temperature (pvT) | |||
| Reinforced | 10% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
300°C/1.2 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 60x60x2 mm; 500 bar |
Flow | ***~*** % | ISO 2577 | |
Across Flow | *** % | ISO 294-4 | 60x60x2 mm; 500 bar |
Across Flow | ***~*** % | ISO 2577 | |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
Water Absorption | *** % | ISO 62 | Saturation, 23°C |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
Filled/Ash | *** % | ISO 3451 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 5 mm/min |
Break | *** Mpa | ISO 527-1/-2 | 5 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 5 mm/min |
Break | *** % | ISO 527-1/-2 | 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2 mm/min |
3.5% strain | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strain | |||
- | *** % | ISO 178 | 2 mm/min |
Tensile Creep Modulus | |||
1h | *** Mpa | ISO 899-1 | |
1000h | *** Mpa | ISO 899-1 | |
Puncture | |||
Force | *** N | ISO 6603-2 | -30℃ |
Force | *** N | ISO 6603-2 | 23℃ |
Energy | *** J | ISO 6603-2 | -30℃ |
Energy | *** J | ISO 6603-2 | 23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | 3 mm,complete break |
Charpy Unnotched Impact Strengh | |||
-60℃ (-76℉) | *** kJ/m² | ISO 179/1eU | complete break |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | complete break |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | complete break |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/A | 3 mm,complete break |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 120 °C/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 50°C/h |
Relative Temperature Index(RTI), Imp | |||
1.5/1.6 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
1.5/1.6 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
1.5/1.6 mm | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Thermal Conductivity | *** W/(m K) | ISO 8302 | cross-flow |
Ball Pressure Test | *** °C | IEC 60695-10-2 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589 | Method A |
Glow Wire Flammability Index(GWFI) | |||
0.75mm | *** °C | IEC 60695-2-12 | |
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.75mm | *** °C | IEC 60695-2-13 | |
1.5mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
FMVSS | *** pass | FMVSS 302 | >=1.0 mm |
Needle Flame Test | *** sec | IEC 60695-11-5 | Method F; 1.5 mm |
Needle Flame Test | *** sec | IEC 60695-11-5 | Method F; 2.0 mm |
Needle Flame Test | *** sec | IEC 60695-11-5 | Method F; 3.0 mm |
Needle Flame Test | *** sec | IEC 60695-11-5 | Method K; 1.5 mm |
Needle Flame Test | *** sec | IEC 60695-11-5 | Method K; 2.0 mm |
Needle Flame Test | *** sec | IEC 60695-11-5 | Method K; 3.0 mm |
Flash ignition temperature | *** °C | ASTM D 1929 | |
Self ignition temperature | *** °C | ASTM D 1929 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
100Hz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Solution B | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | 1 mm |
Electrolytical Corrosion | *** - | IEC 60426 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.