MVR (300°C/1.2 kg) 5.0 cm³/10 min; medical devices; suitable for ETO and steam sterilization at 121°C; biocompatible according to many ISO 10993-1 test requirements; high viscosity; injection molding - melt temperature 290 - 330°C; available in transparent and opaque colors
| Original Document | Technical Datasheet-ISO(English) Technical Datasheet-ISO(Chinese) | |||
| Resin ID | PC FR | |||
| Features | Medical Application/Health CareBiocompatibleEtO sterilizableSteam ResistantHigh Viscosity | |||
| Appearance | Pellets/GranulesClear/TransparentOpaque Color | |||
| Processing | Injection | |||
| Compliance | ISO10993 | |||
| Diagrams | Viscosity-shear rateShearstress-shear rate | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
300°C/1.2 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 60x60x2 mm; 500 bar |
Flow | ***~*** % | ISO 2577 | |
Across Flow | *** % | ISO 294-4 | 60x60x2 mm; 500 bar |
Across Flow | ***~*** % | ISO 2577 | |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
Water Absorption | *** % | ISO 62 | Saturation, 23°C |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Break | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Break | *** % | ISO 527-1/-2 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2 mm/min |
3.5% strain | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strain | |||
- | *** % | ISO 178 | 2 mm/min |
Tensile Creep Modulus | |||
1h | *** Mpa | ISO 899-1 | |
1000h | *** Mpa | ISO 899-1 | |
Puncture | |||
Force | *** N | ISO 6603-2 | -30℃ |
Force | *** N | ISO 6603-2 | 23℃ |
Energy | *** J | ISO 6603-2 | -30℃ |
Energy | *** J | ISO 6603-2 | 23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | 3 mm,complete break |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | 3 mm,partial break |
Charpy Unnotched Impact Strengh | |||
-60℃ (-76℉) | *** kJ/m² | ISO 179/1eU | |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | 3 mm,complete break |
23℃ (73℉) | *** kJ/m² | ISO 180/A | 3 mm,partial break |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 120 °C/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 50°C/h |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Glass Transition Temperature | *** °C | ISO 11357-1/-2 | 10°C/min |
Thermal Conductivity | *** W/(m K) | ISO 8302 | cross-flow |
Ball Pressure Test | *** °C | IEC 60695-10-2 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Oxygen Index | *** % | ISO 4589 | Method A |
Flash ignition temperature | *** °C | ASTM D 1929 | |
Self ignition temperature | *** °C | ASTM D 1929 | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | ISO 13468-2 | 1 mm |
Light Transmission | *** % | ISO 13468-2 | 2 mm |
Light Transmission | *** % | ISO 13468-2 | 3 mm |
Light Transmission | *** % | ISO 13468-2 | 4 mm |
Haze | *** % | ISO 14782 | 3 mm |
Refractive Index | *** - | ISO 489 | Procedure A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.