(PC+ABS)-Blend; flame retardant; Vicat/B 120 = 118°C; UL recognition 94 V-0 at 1.5 mm
| Original Document | Technical Datasheet-ISO(English) Technical Datasheet-ISO(Chinese) | |||
| Features | Flame Retardant | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
260°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 2577 | 150x105x3 mm |
Across Flow | ***~*** % | ISO 2577 | 150x105x3 mm |
Viscosity | *** Pa-s | ISO 11443 | 1000 s-1; 260 °C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Break | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Break | *** % | ISO 527-1/-2 | 50 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/U | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 50 °C/h |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
5VB | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
1.5mm | *** °C | IEC 60695-2-12 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Surface Resistivity | *** Ohm | IEC 60093 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.