PPE+PS blend. 17% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL746C f1. Radiant panel listing. Dielectric strength. Dimensional stability. Suitable for E/E market indoor/outdoor applications including electrical ceiling boxes and smoke detectors.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantCl- FreeBr- FreeDimensional StabilityFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Reinforced | 17% Mineral | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
280°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
300°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
280°C/5.0 kg | *** g/10 min | ASTM D 1238 | |
300°C/5.0 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 3.2 mm |
Outdoor Suitability UL F1/F2 | |||
F1 | *** - | UL 746C | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Yield | *** Mpa | ISO 527 | |
Break | *** Mpa | ISO 527 | |
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | |
Yield | *** % | ISO 527 | |
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Break | *** % | ISO 527 | |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Modulus | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Break | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/2C | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
Instrumented Impact Energy | |||
23℃ (73℉)Total Energy | *** J | ASTM D3763 | |
Reverse Impact | |||
Izod, notched 23°C | *** kJ/m² | ASTM D 256 | 3.2 mm |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | Rate B/120 |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | Rate B/50 |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Radiant Panel Listing | *** - | UL Tested | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Surface Resistivity | *** Ohm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
50/60 Hz | *** - | ASTM D150 | |
1MHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
50/60 Hz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | ASTM D150 | |
Comparative Tracking Index (CTI) | |||
- | *** PLC | UL 746A | |
Dielectric Strength | *** kV/mm | ASTM D149 | in oil, 3.2 mm |
Arc Resistance | *** PLC | ASTM D495 | Tungsten |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746A | |
Hot Wire Ignition(HWI) | PLC | UL 746A | |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746A | surface |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.